Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working
The wrought aluminum alloy 2219 was developed using an induction furnace followed by forging and hot rolling for the improvement of properties. Then the alloy was solution treated at 535 ˚C for 48 minutes followed by water quenched and then aged at 210˚C, 230 ˚C and 240 ˚C for different time period....
Saved in:
Main Authors: | , , , , |
---|---|
Format: | Citation Index Journal |
Published: |
Asian Network for Scientific Information
2011
|
Subjects: | |
Online Access: | http://eprints.utp.edu.my/5141/1/2219_Al__alloy_%28JAS2011%29.ppt.pdf http://eprints.utp.edu.my/5141/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.utp.eprints.5141 |
---|---|
record_format |
eprints |
spelling |
my.utp.eprints.51412017-01-19T08:23:17Z Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working M. Rafi Raza, Rafi Faiz Ahmad , Faiz N.Ikram, Nazma R.Ahmad, Rafiq A.salam, Salam TJ Mechanical engineering and machinery The wrought aluminum alloy 2219 was developed using an induction furnace followed by forging and hot rolling for the improvement of properties. Then the alloy was solution treated at 535 ˚C for 48 minutes followed by water quenched and then aged at 210˚C, 230 ˚C and 240 ˚C for different time period. The maximum tensile strength of 411 MPa and hardness of 113.7 HV were achieved at 210 ˚C after 4 hrs aging. The tensile strength of 368.12 MPa and hardness of 95.32 HV were obtained at 240 ˚C after only 1.5 hrs aging time. The strength and hardness values of aged alloy specimens obtained in this work were reasonably higher (strength 51% and hardness 81%) than the specimens which were solution treated and quenched. Microstructures of the aged specimens also provided an evidence of dispersion of second phase precipitates particles in the single phase matrix. Asian Network for Scientific Information 2011 Citation Index Journal PeerReviewed application/pdf http://eprints.utp.edu.my/5141/1/2219_Al__alloy_%28JAS2011%29.ppt.pdf M. Rafi Raza, Rafi and Faiz Ahmad , Faiz and N.Ikram, Nazma and R.Ahmad, Rafiq and A.salam, Salam (2011) Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working. [Citation Index Journal] http://eprints.utp.edu.my/5141/ |
institution |
Universiti Teknologi Petronas |
building |
UTP Resource Centre |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Teknologi Petronas |
content_source |
UTP Institutional Repository |
url_provider |
http://eprints.utp.edu.my/ |
topic |
TJ Mechanical engineering and machinery |
spellingShingle |
TJ Mechanical engineering and machinery M. Rafi Raza, Rafi Faiz Ahmad , Faiz N.Ikram, Nazma R.Ahmad, Rafiq A.salam, Salam Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working |
description |
The wrought aluminum alloy 2219 was developed using an induction furnace followed by forging and hot rolling for the improvement of properties. Then the alloy was solution treated at 535 ˚C for 48 minutes followed by water quenched and then aged at 210˚C, 230 ˚C and 240 ˚C for different time period. The maximum tensile strength of 411 MPa and hardness of 113.7 HV were achieved at 210 ˚C after 4 hrs aging. The tensile strength of 368.12 MPa and hardness of 95.32 HV were obtained at 240 ˚C after only 1.5 hrs aging time. The strength and hardness values of aged alloy specimens obtained in this work were reasonably higher (strength 51% and hardness 81%) than the specimens which were solution treated and quenched. Microstructures of the aged specimens also provided an evidence of dispersion of second phase precipitates particles in the single phase matrix. |
format |
Citation Index Journal |
author |
M. Rafi Raza, Rafi Faiz Ahmad , Faiz N.Ikram, Nazma R.Ahmad, Rafiq A.salam, Salam |
author_facet |
M. Rafi Raza, Rafi Faiz Ahmad , Faiz N.Ikram, Nazma R.Ahmad, Rafiq A.salam, Salam |
author_sort |
M. Rafi Raza, Rafi |
title |
Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working |
title_short |
Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working |
title_full |
Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working |
title_fullStr |
Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working |
title_full_unstemmed |
Development and Working and Heat treatment strengthening of 2219 Aluminum alloy by mechanical working |
title_sort |
development and working and heat treatment strengthening of 2219 aluminum alloy by mechanical working |
publisher |
Asian Network for Scientific Information |
publishDate |
2011 |
url |
http://eprints.utp.edu.my/5141/1/2219_Al__alloy_%28JAS2011%29.ppt.pdf http://eprints.utp.edu.my/5141/ |
_version_ |
1738655390264983552 |
score |
13.160551 |