Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish
The growth of an intermetallic compound (IMC) can influence the behavior of solder joints. In this study, the different percentages of Ag in Sn-xAg (value x = 2.5 and 3.5 wt.%) solder alloy were involved along with ENImAg surface finish to reveal the solder joints reliability in term of IMC thicknes...
Saved in:
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
WARSE
2020
|
Subjects: | |
Online Access: | http://eprints.uthm.edu.my/6341/1/AJ%202020%20%28818%29.pdf http://eprints.uthm.edu.my/6341/ https://doi.org/10.30534/ijeter/2020/0881.22020 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.uthm.eprints.6341 |
---|---|
record_format |
eprints |
spelling |
my.uthm.eprints.63412022-01-30T03:49:23Z http://eprints.uthm.edu.my/6341/ Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish Mohamed Anuar, Rabiatul Adawiyah Hamidin, Mohamad Shahrom Osman, Saliza Azlina Othman, Mohamad Hilmi TP155-156 Chemical engineering The growth of an intermetallic compound (IMC) can influence the behavior of solder joints. In this study, the different percentages of Ag in Sn-xAg (value x = 2.5 and 3.5 wt.%) solder alloy were involved along with ENImAg surface finish to reveal the solder joints reliability in term of IMC thickness, morphology and strength of solder joint under reflow and multiple reflows. The characterization and samples analysis were examined by OM and SEM/EDX. The observation revealed that the IMC of Sn-xAg/ENImAg which were formed on the interface were Ni3Sn4 and NiSn-P layer after multiple reflows soldering. The kinetic growth of each IMC was observed. It revealed that the layer of IMC was thicker as the reflow increased and became thinner with higher mass percentages of Ag. For solder joint strength, the fracture surface with ductile characteristics at the Sn-Ag/ENImAg interface, which indicated that an increase of Ag wt.% in the solder, increases the strength of the solder joint. Upon the revelation of these observations, the reliability of the solder joint is related to the reflow condition and mass percentages of the element in the solder alloy. WARSE 2020 Article PeerReviewed text en http://eprints.uthm.edu.my/6341/1/AJ%202020%20%28818%29.pdf Mohamed Anuar, Rabiatul Adawiyah and Hamidin, Mohamad Shahrom and Osman, Saliza Azlina and Othman, Mohamad Hilmi (2020) Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish. International Journal of Emerging Trends in Engineering Research, 8 (1). pp. 52-59. ISSN 2347-3983 https://doi.org/10.30534/ijeter/2020/0881.22020 |
institution |
Universiti Tun Hussein Onn Malaysia |
building |
UTHM Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Tun Hussein Onn Malaysia |
content_source |
UTHM Institutional Repository |
url_provider |
http://eprints.uthm.edu.my/ |
language |
English |
topic |
TP155-156 Chemical engineering |
spellingShingle |
TP155-156 Chemical engineering Mohamed Anuar, Rabiatul Adawiyah Hamidin, Mohamad Shahrom Osman, Saliza Azlina Othman, Mohamad Hilmi Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish |
description |
The growth of an intermetallic compound (IMC) can influence the behavior of solder joints. In this study, the different percentages of Ag in Sn-xAg (value x = 2.5 and 3.5 wt.%) solder alloy were involved along with ENImAg surface finish to reveal the solder joints reliability in term of IMC thickness, morphology and strength of solder joint under reflow and multiple reflows. The characterization and samples analysis were examined by OM and SEM/EDX. The observation revealed that the IMC of Sn-xAg/ENImAg which were formed on the interface were Ni3Sn4 and NiSn-P layer after multiple reflows soldering. The kinetic growth of each IMC was observed. It revealed that the layer of IMC was thicker as the reflow increased and became thinner with higher mass percentages of Ag. For solder joint strength, the fracture surface with ductile characteristics at the Sn-Ag/ENImAg interface, which indicated that an increase of Ag wt.% in the solder, increases the strength of the solder joint. Upon the revelation of these observations, the reliability of the solder joint is related to the reflow condition and mass percentages of the element in the solder alloy. |
format |
Article |
author |
Mohamed Anuar, Rabiatul Adawiyah Hamidin, Mohamad Shahrom Osman, Saliza Azlina Othman, Mohamad Hilmi |
author_facet |
Mohamed Anuar, Rabiatul Adawiyah Hamidin, Mohamad Shahrom Osman, Saliza Azlina Othman, Mohamad Hilmi |
author_sort |
Mohamed Anuar, Rabiatul Adawiyah |
title |
Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish |
title_short |
Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish |
title_full |
Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish |
title_fullStr |
Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish |
title_full_unstemmed |
Intermetallic compound layer growth at the Interface between Sn-Ag and ENImAg surface finish |
title_sort |
intermetallic compound layer growth at the interface between sn-ag and enimag surface finish |
publisher |
WARSE |
publishDate |
2020 |
url |
http://eprints.uthm.edu.my/6341/1/AJ%202020%20%28818%29.pdf http://eprints.uthm.edu.my/6341/ https://doi.org/10.30534/ijeter/2020/0881.22020 |
_version_ |
1738581480226947072 |
score |
13.18916 |