Stress corrosion cracking of steel and aluminum in sodium hydroxide: field failure and laboratory test
Through an investigation of the field failure analysis and laboratory experiment, a study on (stress corrosion cracking) SCC behavior of steel and aluminum was performed. All samples were extracted from known operating conditions from the field failures. Similar but accelerated laboratory test was s...
Saved in:
Main Authors: | Prawoto, Yunan, Sumeru, Kasni, Wan Nik, Wan Mohd. Norsani |
---|---|
Format: | Article |
Language: | English |
Published: |
Hindawi Publishing Corporation
2012
|
Subjects: | |
Online Access: | http://eprints.utm.my/id/eprint/25995/1/YunanPrawoto2012_StressCorrosionCrackingofSteelandAluminum.pdf http://eprints.utm.my/id/eprint/25995/ http://dx.doi.org/10.1155/2012/235028 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Similar Items
-
Stress corrosion cracking of steel and aluminumin sodium hydroxide: field failure and laboratory test
by: Prawoto, Yunan, et al.
Published: (2012) -
Effect of prior austenite grain size on the morphology and mechanical properties of martensite in medium carbon steel
by: Prawoto, Yunan, et al.
Published: (2012) -
Incorporating the morphological difference of corrosion cracks in computational fracture mechanics approach
by: Prawoto, Yunan
Published: (2012) -
Effect of pH and chloride concentration on the corrosion of duplex stainless steel
by: Prawoto, Yunan, et al.
Published: (2009) -
The effect of silicon composition on corrosion behavior of aluminum die-cast
by: Prawoto, Yunan, et al.
Published: (2010)