Stress corrosion cracking of steel and aluminum in sodium hydroxide: field failure and laboratory test
Through an investigation of the field failure analysis and laboratory experiment, a study on (stress corrosion cracking) SCC behavior of steel and aluminum was performed. All samples were extracted from known operating conditions from the field failures. Similar but accelerated laboratory test was s...
Saved in:
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Hindawi Publishing Corporation
2012
|
Subjects: | |
Online Access: | http://eprints.utm.my/id/eprint/25995/1/YunanPrawoto2012_StressCorrosionCrackingofSteelandAluminum.pdf http://eprints.utm.my/id/eprint/25995/ http://dx.doi.org/10.1155/2012/235028 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Through an investigation of the field failure analysis and laboratory experiment, a study on (stress corrosion cracking) SCC behavior of steel and aluminum was performed. All samples were extracted from known operating conditions from the field failures. Similar but accelerated laboratory test was subsequently conducted in such a way as to mimic the field failures. The crack depth and behavior of the SCC were then analyzed after the laboratory test and the mechanism of stress corrosion cracking was studied. The results show that for the same given stress relative to ultimate tensile strength, the susceptibility to SCC is greatly influenced by heat treatment. Furthermore, it was also concluded that when expressed relative to the (ultimate tensile strength) UTS, aluminum has similar level of SCC susceptibility to that of steel, although with respect to the same absolute value of applied stress, aluminum is more susceptible to SCC in sodium hydroxide environment than steel. |
---|