In vitro surface efficacy of CaP-based anodised titanium for bone implants
This study examined the effect of changes to the surface of CaP-based anodised titanium on osteogenesis and antimicrobial activity in vitro. The present work is proposed to investigate the mechanical stability of two different CaP/TiO2 micromorphology-based coatings, namely donut-shaped (350 V) and...
Saved in:
Main Authors: | , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2023
|
Subjects: | |
Online Access: | http://eprints.uthm.edu.my/9515/1/J16043_3ebf01813a855fc8bfbea2ea2e595eb8.pdf http://eprints.uthm.edu.my/9515/ https://doi.org/10.1016/j.surfin.2023.102872 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | This study examined the effect of changes to the surface of CaP-based anodised titanium on osteogenesis and
antimicrobial activity in vitro. The present work is proposed to investigate the mechanical stability of two different CaP/TiO2 micromorphology-based coatings, namely donut-shaped (350 V) and needle-shaped (450 V), that are fabricated by single-step micro-arc anodic oxidation at different conditions alongside with their cytocompatibility and antibacterial properties. The microhardness of the sample anodised at 450 V is ~100 MPa lower than that seen in the sample fabricated at 350 V, but both resultant coatings were strongly adhere to the substrate. However, the coating at 450 V was observed to suffer from delamination, indicating the needle-like
structure is mechanically unstable. After 7 days of SBF immersion, the 450 V sample was highly bioactive
relative to the 350 V sample. However, MTT assays showed that the 450 V coatings showed lower growth rate of
hFOB 1.19 at day 14, which indicates that although the structure does have a superior ability to form apatite, it
has long-term negative implications possibly from the toxicity of the structure to bone growth. The Alizarin-red staining shows that 450 V sample shows a negative trend of osteogenic mineralisation, thus qualitatively validating the toxicity. For antimicrobial effects, the donut-shaped microstructures were shown to have adequate antibacterial properties compared to the needle-like structures. Overall, this study suggest that the donut-shaped TiO2 morphology is the best cementless interface for bone cell anchorage. |
---|