The critical current density of polycrystalline MgB2 prepared by using boron mixture
In this study, boron powders with varying purity and form were mixed in different proportion to serve as precursors for reaction with Mg forming polycrystalline MgB2 bulks. The inductively measured superconducting transition temperature, Tc and the critical current density, J c were compared to that...
Saved in:
Main Authors: | , |
---|---|
Format: | Article |
Language: | English English |
Published: |
IEEE
2009
|
Online Access: | http://psasir.upm.edu.my/id/eprint/8864/1/The%20critical%20current%20density%20of%20polycrystalline%20MgB2%20prepared%20by%20using%20boron%20mixture.pdf http://psasir.upm.edu.my/id/eprint/8864/ http://dx.doi.org/10.1109/TASC.2009.2018461 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.upm.eprints.8864 |
---|---|
record_format |
eprints |
spelling |
my.upm.eprints.88642015-11-03T07:53:03Z http://psasir.upm.edu.my/id/eprint/8864/ The critical current density of polycrystalline MgB2 prepared by using boron mixture Chen, Soo Kien MacManus-Driscoll, Judith L. In this study, boron powders with varying purity and form were mixed in different proportion to serve as precursors for reaction with Mg forming polycrystalline MgB2 bulks. The inductively measured superconducting transition temperature, Tc and the critical current density, J c were compared to that of samples prepared from the respective single boron. Overall, Tc remains largely unchanged for all samples. It was found that Jc at 6 K and 20 K did not degrade significantly up to 4.6 T as a result of adding impure boron as much as 10 wt.% indicating comparable Jc can be obtained without dependence of use of expensive high purity boron powder alone. The systematic decrease of Jc with increasing impure boron additions shows that a compromise between desired and cost reduction can be made by varying the boron powder proportion. Finally, samples prepared from the mixture of both impure crystalline and amorphous borons even show enhanced Jc up to 3 T at 20 K. The increase in Jc correlates with the retention of strain level in these samples probably resulted from the more similar reaction rate of the respective borons. IEEE 2009-06 Article NonPeerReviewed application/pdf en http://psasir.upm.edu.my/id/eprint/8864/1/The%20critical%20current%20density%20of%20polycrystalline%20MgB2%20prepared%20by%20using%20boron%20mixture.pdf Chen, Soo Kien and MacManus-Driscoll, Judith L. (2009) The critical current density of polycrystalline MgB2 prepared by using boron mixture. IEEE Transactions on Applied Superconductivity, 19 (3). pp. 2771-2774. ISSN 1051-8223 http://dx.doi.org/10.1109/TASC.2009.2018461 10.1109/TASC.2009.2018461 English |
institution |
Universiti Putra Malaysia |
building |
UPM Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Putra Malaysia |
content_source |
UPM Institutional Repository |
url_provider |
http://psasir.upm.edu.my/ |
language |
English English |
description |
In this study, boron powders with varying purity and form were mixed in different proportion to serve as precursors for reaction with Mg forming polycrystalline MgB2 bulks. The inductively measured superconducting transition temperature, Tc and the critical current density, J c were compared to that of samples prepared from the respective single boron. Overall, Tc remains largely unchanged for all samples. It was found that Jc at 6 K and 20 K did not degrade significantly up to 4.6 T as a result of adding impure boron as much as 10 wt.% indicating comparable Jc can be obtained without dependence of use of expensive high purity boron powder alone. The systematic decrease of Jc with increasing impure boron additions shows that a compromise between desired and cost reduction can be made by varying the boron powder proportion. Finally, samples prepared from the mixture of both impure crystalline and amorphous borons even show enhanced Jc up to 3 T at 20 K. The increase in Jc correlates with the retention of strain level in these samples probably resulted from the more similar reaction rate of the respective borons. |
format |
Article |
author |
Chen, Soo Kien MacManus-Driscoll, Judith L. |
spellingShingle |
Chen, Soo Kien MacManus-Driscoll, Judith L. The critical current density of polycrystalline MgB2 prepared by using boron mixture |
author_facet |
Chen, Soo Kien MacManus-Driscoll, Judith L. |
author_sort |
Chen, Soo Kien |
title |
The critical current density of polycrystalline MgB2 prepared by using boron mixture |
title_short |
The critical current density of polycrystalline MgB2 prepared by using boron mixture |
title_full |
The critical current density of polycrystalline MgB2 prepared by using boron mixture |
title_fullStr |
The critical current density of polycrystalline MgB2 prepared by using boron mixture |
title_full_unstemmed |
The critical current density of polycrystalline MgB2 prepared by using boron mixture |
title_sort |
critical current density of polycrystalline mgb2 prepared by using boron mixture |
publisher |
IEEE |
publishDate |
2009 |
url |
http://psasir.upm.edu.my/id/eprint/8864/1/The%20critical%20current%20density%20of%20polycrystalline%20MgB2%20prepared%20by%20using%20boron%20mixture.pdf http://psasir.upm.edu.my/id/eprint/8864/ http://dx.doi.org/10.1109/TASC.2009.2018461 |
_version_ |
1643824143698755584 |
score |
13.18916 |