EPRB423 Project II Measurement of the transport critical current in thallium-1212 tapes at 77k using the 1uV/cm criteria
Ag-sheathed T1-1212 tapes with a nominal composition of (T1Cr)SrCaCuO were fabricated using the powder-in-tube (PIT) method. Two sets of samples were annealed in oxygen flow at 800C and 890C each for 30 minutes. Another set was annealed at 800C for 1 hour. The tapes showed transition temperature, T...
Saved in:
| Main Author: | |
|---|---|
| Format: | text::Thesis |
| Language: | English |
| Published: |
2023
|
| Subjects: | |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Ag-sheathed T1-1212 tapes with a nominal composition of (T1Cr)SrCaCuO were fabricated using the powder-in-tube (PIT) method. Two sets of samples were annealed in oxygen flow at 800C and 890C each for 30 minutes. Another set was annealed at 800C for 1 hour. The tapes showed transition temperature, T between 80K to 100K. |
|---|