Influence of annealing temperature on the sensitivity of nickel oxide nanosheet films in humidity sensing applications

• Main Authors: Norfarariyanti Parimon, M. H. Mamat, A. S. Ismail, I. B. Shameem Banu, M. K. Ahmad, A. B. Suriani, M. Rusop
• Format: Article
• Language: English; English
• Published: Institute of Advanced Engineering and Science (IAES) 2020
• Subjects: TK7800-8360 Electronics
• Online Access: https://eprints.ums.edu.my/id/eprint/30990/1/Influence%20of%20annealing%20temperature%20on%20the%20sensitivity%20of%20nickel%20oxide%20nanosheet%20films%20in%20humidity%20sensing%20applications_ABSTRACT.pdf; https://eprints.ums.edu.my/id/eprint/30990/2/Influence%20of%20annealing%20temperature%20on%20the%20sensitivity%20of%20nickel%20oxide%20nanosheet%20films%20in%20humidity%20sensing%20applications.pdf; https://eprints.ums.edu.my/id/eprint/30990/; http://ijeecs.iaescore.com/index.php/IJEECS/article/view/21119; http://doi.org/10.11591/ijeecs.v18.i1.pp284-292

Nickel oxide (NiO) nanosheet films were successfully grown onto NiO seed-coated glass substrates at different annealing temperatures for humidity sensing applications. NiO seed layers and NiO nanosheet films were prepared using a sol-gel spin coating and sonicated sol-gel immersion techniques, respectively. The properties of NiO nanosheet films at as-deposited, 300 ℃, and 500 ℃-annealed were examined by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), ultraviolet-visible (UV-vis) spectroscopy, and humidity sensor measurement system. The XRD patterns demonstrate that the grown NiO films have crystalline cubic structures at temperature of 300 ℃ and 500 ℃. The FESEM images show that the large porous nanosheet network spread over the layers as the annealing temperature increased. The UV-vis spectra revealed that all the nanosheet films have the average transmittance below than 50% in the visible region, with absorption edges ~ 350 nm. The optical band gap energy was evaluated in ranges of 3.39 to 3.61 eV. From the obtained humidity sensing results, it shows that 500 ℃-annealed film exhibited the best sensitivity of 257, as well as the slowest response time, and the fastest recovery time compared with others.