Fabrication of nickel-cobalt intermetallic nanotapes by electrospinning
This dissertation thesis is on the fabrication of Nickel-Cobalt nanotapes prepared by electrospinning technique. Electrospinning is a nanofabrication technique in which a polymeric solution is allowed to pass through an electric field of intensity ~105 V/m. In this work, the precursor polymeric sol...
Saved in:
| Main Author: | |
|---|---|
| Format: | Undergraduates Project Papers |
| Language: | English |
| Published: |
2016
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/19272/1/Fabrication%20of%20nickel-cobalt%20intermetallic%20nanotapes%20by%20electrospinning.pdf http://umpir.ump.edu.my/id/eprint/19272/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This dissertation thesis is on the fabrication of Nickel-Cobalt nanotapes prepared by electrospinning technique. Electrospinning is a nanofabrication technique in which a
polymeric solution is allowed to pass through an electric field of intensity ~105 V/m. In this work, the precursor polymeric solution was prepared by dissolving equimolar
nickel acetate (18 mmol) and cobalt acetate in 50 wt.% polyvinylpyrrolidone (Mol. Wt. 40,000) in ethanol. The viscosity of the above solution was measured using a
viscometer; the viscosity of the solution was ~653 cP. This solution was electrospun using a commercial electrospinning unit at 24 kV with a solution injection rate 0.5 ml/h. The as-spun fibers were annealed in an argon atmosphere at ~450 – 550oC for 1 h, based on thermogravimetric analysis. The annealed materials were examined by X-ray diffraction (XRD) technique and field emission scanning electron microscopy (FESEM). The XRD measurements showed that the annealed samples were only
partially crystallized and has a belt-like morphology. |
|---|