Effect of thermocycling on the compressive strength of selected luting cements
Introduction: The purpose of this in vitro study was to evaluate the effect of thermocycling on the compressive strength of selected luting cements. Material and methods: 5 types of luting cements were tested. A total of thirty cylindrical specimens measuring 6mm in height and 4mm in diameter were p...
Saved in:
Main Authors: | , , |
---|---|
Format: | Article |
Published: |
International Islamic University Malaysia
2018
|
Subjects: | |
Online Access: | http://eprints.um.edu.my/22423/ http://iiumedic.net/imjm/v1/download/volume_17_no_3/Vol17No3-075.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.um.eprints.22423 |
---|---|
record_format |
eprints |
spelling |
my.um.eprints.224232019-09-18T07:35:04Z http://eprints.um.edu.my/22423/ Effect of thermocycling on the compressive strength of selected luting cements Aws Ali Al-Kadhim, H. Abdullah, Hadijah Al-Ani Sarah, T. RK Dentistry Introduction: The purpose of this in vitro study was to evaluate the effect of thermocycling on the compressive strength of selected luting cements. Material and methods: 5 types of luting cements were tested. A total of thirty cylindrical specimens measuring 6mm in height and 4mm in diameter were prepared for each type of cement which were then divided into two groups ie Group 1: Exposure, and Group 2: Control. Both groups were stored in distilled water at 37°C for 24 hours. Group 1 was subjected to 500 cycles in a thermocycling baths of 5°C and 55°C with 20 seconds in each bath. Group 2 was not exposed to thermocycling procedure. The compressive strength for each cement type was determined by using a universal testing machine. Results: Resin adhesive cement had the highest compressive strength; followed by conventional glass ionomer cement (GIC) whilst resin modified GIC was the least. Thermocycling had no significant effect on the compressive strength of RelyX™ ARC and Fuji I (p > 0.05), but a significant effect on Fuji I CAPSULE, Fuji CEM, Fuji Plus CAPSLUE (p < 0.05) was observed. Conclusion: The effect of thermocycling on the compressive strength of luting cements differed considerably with respect to their chemical compositions. International Islamic University Malaysia 2018 Article PeerReviewed Aws Ali Al-Kadhim, H. and Abdullah, Hadijah and Al-Ani Sarah, T. (2018) Effect of thermocycling on the compressive strength of selected luting cements. International Medical Journal Malaysia, 17 (3). pp. 75-80. ISSN 1823-4631 http://iiumedic.net/imjm/v1/download/volume_17_no_3/Vol17No3-075.pdf |
institution |
Universiti Malaya |
building |
UM Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Malaya |
content_source |
UM Research Repository |
url_provider |
http://eprints.um.edu.my/ |
topic |
RK Dentistry |
spellingShingle |
RK Dentistry Aws Ali Al-Kadhim, H. Abdullah, Hadijah Al-Ani Sarah, T. Effect of thermocycling on the compressive strength of selected luting cements |
description |
Introduction: The purpose of this in vitro study was to evaluate the effect of thermocycling on the compressive strength of selected luting cements. Material and methods: 5 types of luting cements were tested. A total of thirty cylindrical specimens measuring 6mm in height and 4mm in diameter were prepared for each type of cement which were then divided into two groups ie Group 1: Exposure, and Group 2: Control. Both groups were stored in distilled water at 37°C for 24 hours. Group 1 was subjected to 500 cycles in a thermocycling baths of 5°C and 55°C with 20 seconds in each bath. Group 2 was not exposed to thermocycling procedure. The compressive strength for each cement type was determined by using a universal testing machine. Results: Resin adhesive cement had the highest compressive strength; followed by conventional glass ionomer cement (GIC) whilst resin modified GIC was the least. Thermocycling had no significant effect on the compressive strength of RelyX™ ARC and Fuji I (p > 0.05), but a significant effect on Fuji I CAPSULE, Fuji CEM, Fuji Plus CAPSLUE (p < 0.05) was observed. Conclusion: The effect of thermocycling on the compressive strength of luting cements differed considerably with respect to their chemical compositions. |
format |
Article |
author |
Aws Ali Al-Kadhim, H. Abdullah, Hadijah Al-Ani Sarah, T. |
author_facet |
Aws Ali Al-Kadhim, H. Abdullah, Hadijah Al-Ani Sarah, T. |
author_sort |
Aws Ali Al-Kadhim, H. |
title |
Effect of thermocycling on the compressive strength of selected luting cements |
title_short |
Effect of thermocycling on the compressive strength of selected luting cements |
title_full |
Effect of thermocycling on the compressive strength of selected luting cements |
title_fullStr |
Effect of thermocycling on the compressive strength of selected luting cements |
title_full_unstemmed |
Effect of thermocycling on the compressive strength of selected luting cements |
title_sort |
effect of thermocycling on the compressive strength of selected luting cements |
publisher |
International Islamic University Malaysia |
publishDate |
2018 |
url |
http://eprints.um.edu.my/22423/ http://iiumedic.net/imjm/v1/download/volume_17_no_3/Vol17No3-075.pdf |
_version_ |
1646210237293658112 |
score |
13.18916 |