Effect of thermocycling on the compressive strength of selected luting cements
Introduction: The purpose of this in vitro study was to evaluate the effect of thermocycling on the compressive strength of selected luting cements. Material and methods: 5 types of luting cements were tested. A total of thirty cylindrical specimens measuring 6mm in height and 4mm in diameter were p...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Published: |
International Islamic University Malaysia
2018
|
| Subjects: | |
| Online Access: | http://eprints.um.edu.my/22423/ http://iiumedic.net/imjm/v1/download/volume_17_no_3/Vol17No3-075.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Introduction: The purpose of this in vitro study was to evaluate the effect of thermocycling on the compressive strength of selected luting cements. Material and methods: 5 types of luting cements were tested. A total of thirty cylindrical specimens measuring 6mm in height and 4mm in diameter were prepared for each type of cement which were then divided into two groups ie Group 1: Exposure, and Group 2: Control. Both groups were stored in distilled water at 37°C for 24 hours. Group 1 was subjected to 500 cycles in a thermocycling baths of 5°C and 55°C with 20 seconds in each bath. Group 2 was not exposed to thermocycling procedure. The compressive strength for each cement type was determined by using a universal testing machine. Results: Resin adhesive cement had the highest compressive strength; followed by conventional glass ionomer cement (GIC) whilst resin modified GIC was the least. Thermocycling had no significant effect on the compressive strength of RelyX™ ARC and Fuji I (p > 0.05), but a significant effect on Fuji I CAPSULE, Fuji CEM, Fuji Plus CAPSLUE (p < 0.05) was observed. Conclusion: The effect of thermocycling on the compressive strength of luting cements differed considerably with respect to their chemical compositions. |
|---|