Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.]
A direct diffusion bonding of marine grade aluminium alloy AA6061 and steel A36 was carried out in an argon environment at 640°C. Specimens were heated in a furnace for a holding time of 90 to 120 min under a pre-pressed condition. An interface microstructural observation revealed an increase in the...
Saved in:
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Faculty of Mechanical Engineering Universiti Teknologi MARA (UiTM)
2018
|
Subjects: | |
Online Access: | http://ir.uitm.edu.my/id/eprint/36294/1/36294.pdf http://ir.uitm.edu.my/id/eprint/36294/ https://jmeche.uitm.edu.my/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.uitm.ir.36294 |
---|---|
record_format |
eprints |
spelling |
my.uitm.ir.362942020-11-06T04:26:45Z http://ir.uitm.edu.my/id/eprint/36294/ Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] Ismail, Asmawi Hussain, Patthi Mustapha, Mazli Nuruddin, Muhd Fadhil TJ Mechanical engineering and machinery A direct diffusion bonding of marine grade aluminium alloy AA6061 and steel A36 was carried out in an argon environment at 640°C. Specimens were heated in a furnace for a holding time of 90 to 120 min under a pre-pressed condition. An interface microstructural observation revealed an increase in the thickness of this reaction layer as bonding time increased. A 33.4 μm thickness was recorded at the interfacial zone of the joint after a 120-min holding time condition. Hardness along the bonding line was measured using a micro-Vickers hardness tester. Diffusion of aluminium and iron was observed on both parent metals at the interfacial zone using scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS). This experiment had proven that different content and thickness of alloy compounds were formed at various reaction time frames on the interfacial zone. Faculty of Mechanical Engineering Universiti Teknologi MARA (UiTM) 2018 Article PeerReviewed text en http://ir.uitm.edu.my/id/eprint/36294/1/36294.pdf Ismail, Asmawi and Hussain, Patthi and Mustapha, Mazli and Nuruddin, Muhd Fadhil (2018) Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.]. Journal of Mechanical Engineering (JMechE), 15 (1). pp. 80-91. ISSN 1823-5514 ; 2550-164X https://jmeche.uitm.edu.my/ |
institution |
Universiti Teknologi Mara |
building |
Tun Abdul Razak Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Teknologi Mara |
content_source |
UiTM Institutional Repository |
url_provider |
http://ir.uitm.edu.my/ |
language |
English |
topic |
TJ Mechanical engineering and machinery |
spellingShingle |
TJ Mechanical engineering and machinery Ismail, Asmawi Hussain, Patthi Mustapha, Mazli Nuruddin, Muhd Fadhil Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] |
description |
A direct diffusion bonding of marine grade aluminium alloy AA6061 and steel A36 was carried out in an argon environment at 640°C. Specimens were heated in a furnace for a holding time of 90 to 120 min under a pre-pressed condition. An interface microstructural observation revealed an increase in the thickness of this reaction layer as bonding time increased. A 33.4 μm thickness was recorded at the interfacial zone of the joint after a 120-min holding time condition. Hardness along the bonding line was measured using a micro-Vickers hardness tester. Diffusion of aluminium and iron was observed on both parent metals at the interfacial zone using scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS). This experiment had proven that different content and thickness of alloy compounds were formed at various reaction time frames on the interfacial zone. |
format |
Article |
author |
Ismail, Asmawi Hussain, Patthi Mustapha, Mazli Nuruddin, Muhd Fadhil |
author_facet |
Ismail, Asmawi Hussain, Patthi Mustapha, Mazli Nuruddin, Muhd Fadhil |
author_sort |
Ismail, Asmawi |
title |
Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] |
title_short |
Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] |
title_full |
Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] |
title_fullStr |
Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] |
title_full_unstemmed |
Fe-Al Diffusion Bonding: Effect of reaction time on the interlayer thickness / Asmawi Ismail...[et al.] |
title_sort |
fe-al diffusion bonding: effect of reaction time on the interlayer thickness / asmawi ismail...[et al.] |
publisher |
Faculty of Mechanical Engineering Universiti Teknologi MARA (UiTM) |
publishDate |
2018 |
url |
http://ir.uitm.edu.my/id/eprint/36294/1/36294.pdf http://ir.uitm.edu.my/id/eprint/36294/ https://jmeche.uitm.edu.my/ |
_version_ |
1685651385476972544 |
score |
13.160551 |