LiVOPO4 as a new cathode materials for Li-ion rechargeable battery
mprovement in the rate properties of orthorhombic LiVOPO4 was investigated and it was found that making a fine powder of LiVOPO4by the mechanical milling pretreatment is effective for increasing the de-intercalation capacity of Li from LiVOPO4. The electrochemical de-intercalation capacity at high c...
Saved in:
Main Authors: | , , , |
---|---|
Format: | Citation Index Journal |
Published: |
Elsevier B.V.
2005
|
Subjects: | |
Online Access: | http://eprints.utp.edu.my/3802/1/Azmi_2005_Journal-of-Power-Sources.pdf http://eprints.utp.edu.my/3802/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | mprovement in the rate properties of orthorhombic LiVOPO4 was investigated and it was found that making a fine powder of LiVOPO4by the mechanical milling pretreatment is effective for increasing the de-intercalation capacity of Li from LiVOPO4. The electrochemical de-intercalation capacity at high current density can further increase by optimizing the acetylene black amount as a conducting binder. Theoptimized acetylene black amount was 15 wt.% and intercalation capacity of Li was achieved a value of 100 and 60 mAh g−1 at high rate
condition of C/5 (0.4mAcm−2) and 1C (2mAcm−2), respectively. |
---|