Interaction of zn2+ with extraframework aluminium in HBEA zeolite and its role in enhancing n-pentane isomerization
The electrodeposition method was used to produce Zn2+ cation precursors, followed by the introduction of Zn2+ cation precursors to HBEA by the ion exchange technique. The introduction of Zn2+ cations slightly changed the specific surface area and crystallinity of HBEA. IR, XPS and solid state MAS NM...
Saved in:
Main Authors: | , , , , , , , |
---|---|
Format: | Article |
Published: |
Elsevier Ltd.
2012
|
Subjects: | |
Online Access: | http://eprints.utm.my/id/eprint/47116/ https://dx.doi.org/10.1016/j.apcata.2012.04.020 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The electrodeposition method was used to produce Zn2+ cation precursors, followed by the introduction of Zn2+ cation precursors to HBEA by the ion exchange technique. The introduction of Zn2+ cations slightly changed the specific surface area and crystallinity of HBEA. IR, XPS and solid state MAS NMR results showed that Zn2+ cations interacted with (AlO)+ extraframework aluminum to form Zn(OAl)2 and simultaneously induced the formation of bridging hydroxyl groups, Si(OH)Al. The pyridine adsorbed IR study revealed that the presence of Zn2+ cations fully eliminated weak and partially eliminated strong Brønsted acid sites. As a result, strong and relatively weak Lewis acid sites were formed in which the pyridine probe molecule desorbed at 623 K and below. The presence of Zn2+ cations enhanced the catalytic activity of HBEA in n-pentane isomerization due to the presence of strong Lewis acid sites; the sites may facilitate the formation and maintenance of active protonic acid sites through a hydrogen spillover mechanism. At 598 K, the yield of isopentane for Zn-HBEA was 25.7% higher than that of HBEA. Within a reaction temperature range of 373–648 K, the apparent activation energy for isomerization of n-pentane over HBEA and Zn-HBEA was 118.76 and 90.79 kJ/mol, respectively. |
---|