Effect of pandanus amaryllifolius fibre on physio-mechanical, thermal and biodegradability of thermoplastic cassava starch/beeswax composites

• Main Authors: Z. N. Diyana, Z. N. Diyana, Jumaidin, R., Selamat, Mohd. Zulkefli, Mohd. Suan, Mohd. Shahadan, Kamaruddin, Zatil Hazrati, Md. Yusof, Fahmi Asyadi, Rushdan, Ahmad Ilyas, Tag Eldin, Elsayed Mohamed
• Format: Article
• Published: Springer Nature 2024
• Subjects: Q Science (General)
• Online Access: http://eprints.utm.my/108917/; http://dx.doi.org/10.1007/s10924-023-03039-x

Pandanus amaryllifolius fibre (PAF) is an agricultural waste plant derived from the natural cellulosic source of fibre that can be used in various bio-material applications. In the present study, a novel biodegradable thermoplastic cassava starch/beeswax blends reinforced with Pandanus amaryllifolius fibre (TCPS/BW/PAF) bio-composites were successfully developed at varied Pandanus amaryllifolius fibre concentrations of 0, 10, 20, 30, 40, 50 and 60 wt% while beeswax loading was remained constant at 2.5 wt% concentration using hot moulding compression method. A comprehensive characterisation of TCPS/BW/PAF bio-composites was examined in terms of their physical, mechanical, thermal and biodegradation properties. The addition of Pandanus amaryllifolius fibre has significantly improved tensile strength and tensile modulus at maximum value obtained 10.9 and 606.5 MPa, respectively as well as flexural strength and flexural modulus of bio-composite at maximum value obtained 21.37 and 523.76 MPa, respectively until 50 wt% Pandanus amaryllifolius fibre loading. Surface morphology of the fractured tensile samples PAF10 to PAF50 shows compacted structure and fibre breakage, indicating effective stress transfer from starch matrix to PAF during tensile force application. Furthermore, the addition of Pandanus amaryllifolius fibre improved thermal stability from TG, DTG and DSC results; improved crystallinity from XRD analysis; reduced water and moisture affinity from physical properties testing, and lowered the biodegradation rate. Overall, this study shows the potential of TCPS/BW/PAF bio-composites in biopolymer application and bio-packaging industries.