Experimental study of fracture energy for foamed concrete
Foamed concrete has recently gained attention as an alternative material to normal concrete in structural engineering. As a structural component, foamed concrete has many advantages given its characteristics such as high strength with low density, good serviceability, and lightweight. Therefore,...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English English English |
Published: |
2021
|
Subjects: | |
Online Access: | http://eprints.uthm.edu.my/6438/1/24p%20ALSAD%20NASRULLAH.pdf http://eprints.uthm.edu.my/6438/2/ALSAD%20NASRULLAH%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/6438/3/ALSAD%20NASRULLAH%20WATERMARK.pdf http://eprints.uthm.edu.my/6438/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Foamed concrete has recently gained attention as an alternative material to normal
concrete in structural engineering. As a structural component, foamed concrete has many
advantages given its characteristics such as high strength with low density, good
serviceability, and lightweight. Therefore, many studies have been investigated for their
strength and mechanical properties. However, literature has shown that there is a lack of
research on fracture energy of foamed concrete, which is the main parameter that governs
damage and cracks mechanisms of any structural components. Therefore, the present
study aims to experimentally investigate the fracture energy of foamed concrete using
beam specimens with U-notch and V-notch through a three-point bending test. Fifty-two
(52) foamed concrete beam specimens with 100 mm x 100 mm x 800 mm in length with
a density of 1600 kg/m³ were cast. The foamed concrete compressive strength of
approximately 9 to 10 MPa was achieved at 28 days. Of the fifty-two numbers of beam
specimens, two beams were cast as control specimens (with no notches) whilst the fortyeight
number
of
beam
specimens
was
provided
with
various
variables
including
different
notch
shapes
(U
and
V-notch),
different
notch
sizes
(notch
depth
to
notch
opening
ratio),
and
different offset ratios. From the three-point bending test, the peak load, loaddisplacement
profile, and crack patterns for all the beam specimens were highly
influenced by the various variables provided. From observation, beams with V-notch with
its single corner edge tip and at offset ratio at 0.0 gave higher peak loads and consistent
crack patterns compared to beams with U-notch. Increasing the offset ratio reduces the
peak load and changes the crack patterns when a combination of shear and bending stress
influences the tensile stresses hence the crack direction of the beam. The experimental
fracture energy GF was determined from the classical Hillerborg’s model. Three other
theoretical models from Bazant, CEB, and JCIS were selected for comparison. For beams
with U-notch, Bazant and CEB overestimated its fracture energy by +11.58% and
+24.18% whilst JCIS underestimated its result by -30.18%. Similar trends was observed
for beams with V-notches when Bazant and CEB both overestimated by +13.33% and
24.48% but was again underestimated by JCIS at -29.16%. However, by modifying the
factors from Bazant, CEB, and JCIS equations, a modified theoretical model to measure
fracture energy for foamed concrete was successfully developed. This was validated when
the modified Bazant, CEB, and JCIS model achieved high accuracy levels at +0.64%,
+0.63%, and +1.24%. |
---|