Optimization of wear and hardness of Al–Zn–Mg–Cu alloy fabricated from recycled beverage can using response surface methodology
A novel X7475 (Al–Zn–Mg–Cu) alloy was fabricated from recycled beverage cans (RBCs). Al was recovered from RBC. Zn and Mn were sourced from spent batteries, while Cu was sourced from copper wire. The weight percent (wt%) Zn was varied at 4, 4.5 and 5. Following the fabrication of rods, samples were...
Saved in:
Main Authors: | Kazeem, Abubakar, Badarulzaman, Nur Azam, Wan Ali, Wan Fahmin Faiz |
---|---|
Format: | Article |
Language: | English |
Published: |
Springer
2020
|
Subjects: | |
Online Access: | http://eprints.uthm.edu.my/6387/1/AJ%202020%20%28314%29.pdf http://eprints.uthm.edu.my/6387/ https://doi.org/10.1007/s42452-020-2836-7 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Similar Items
-
Optimization of wear and hardness of al Al–Zn–Mg–Cu alloy fabricated from recycled beverage can using response surface methodology
by: Kazeem, Abubakar, et al.
Published: (2020) -
Effect of imperfections on and modelling of conductivity and hardness of high-Zn X7xxx cast al-alloys produced from recycled beverage can
by: Kazeem, Abubakar, et al.
Published: (2020) -
Relating fractographic analysis to yield strength of novel X7475 (Al–Zn–Mg–Cu) alloys produced by recycling aluminium beverage cans
by: Kazeem, Abubakar, et al.
Published: (2020) -
Relating fractographic analysis to yield strength of novel X7475
(Al–Zn–Mg–Cu) alloys produced by recycling aluminium beverage cans
by: Kazeem, Abubakar, et al.
Published: (2020) -
Effect of annealing and artificial ageing parameters on the ultimate tensile strength and elongation of new Al-(4-5) Zn- Mg-Mn-Cu alloys fabricated using recycled beverage cans
by: Kazeem, Abubakar, et al.
Published: (2020)