The influenced of steel fiber in hot mix asphalt mixture to enhance the tensile strength

Deformation of the road was the main factor of the repeated loaded at high temperature to the asphalt pavements and one of the main distress mechanisms. Asphalt mixture incorporated with steel fiber to enhance the tensile strength would have investigated by used grade 60/70 of asphalt binder and...

وصف كامل

محفوظ في:
التفاصيل البيبلوغرافية
المؤلفون الرئيسيون: Mohd Syukry, Safwan, Haiqal Azizan, Muhammad Daniel, Sobri, Muhammad Salleh, Bujang, Hazirah
التنسيق: Conference or Workshop Item
اللغة:English
منشور في: 2024
الموضوعات:
الوصول للمادة أونلاين:http://eprints.uthm.edu.my/10862/1/P16562_c999e55542985d2247ed771eb2e0a729.pdf
http://eprints.uthm.edu.my/10862/
https://doi.org/10.30880/mari.2024.05.01.022
الوسوم: إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
الوصف
الملخص:Deformation of the road was the main factor of the repeated loaded at high temperature to the asphalt pavements and one of the main distress mechanisms. Asphalt mixture incorporated with steel fiber to enhance the tensile strength would have investigated by used grade 60/70 of asphalt binder and 5% of optimum asphalt binder. The percentages of steel fiber that were used for the studied was 0, 1.2, 1.5, 2.1, 2.4% by total weight of aggregate. Purpose of this studied is to investigate the effect of steel fiber toward the asphalt mixture on improved the asphalt pavement. To decrease the road deformation and to compute the pavement cracked at incorporating steel fiber using Marshall Stability Test. The result from this study has shown that the mixture incorporating steel fibers for stability is decrease between control sample with 2.7% steel fiber which is 21.357 kN and 13.193 kN. The performance test due to stiffness analysis passed the requirement JKR, which is more than 2.6 kN/mm, even if the value of the steel fiber modified sample is lower than the control sample and it still relevance to implement