Lightweight And Green Tiles From Recycled Polypropylene Reinforced With Cockle-Shells Powder
Fabrication of recycled polypropylene filled with cockle-shells composite tiles via melt compounding and hot pressing method were studied.Cockles-shell powder reinforced polypropylene composites were sieved within particle size range of 63µm – 75µm for different weight ratio of 0 wt%,5 wt%,10 wt%,20...
Saved in:
Main Authors: | , , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Universiti Teknikal Malaysia Melaka
2017
|
Subjects: | |
Online Access: | http://eprints.utem.edu.my/id/eprint/21607/2/IRID2017_Lightweight.pdf http://eprints.utem.edu.my/id/eprint/21607/ http://amc.utem.edu.my/index.php?option=com_docman&view=download&alias=53-p41-60&category_slug=irid2016&Itemid=144 http://amc.utem.edu.my/index.php?option=com_docman&view=list&slug=irid2016&Itemid=144 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Fabrication of recycled polypropylene filled with cockle-shells composite tiles via melt compounding and hot pressing method were studied.Cockles-shell powder reinforced polypropylene composites were sieved within particle size range of 63µm – 75µm for different weight ratio of 0 wt%,5 wt%,10 wt%,20 wt%,25 wt% and 30 wt%. Tensile properties was selected as the response.The fracture surface of cockle-hells composite tiles,then were further verified using scanning electron microscopy and fourier transimission infrared radiation.The increasing of cockles-shells powder weight percentage, decrease the tensile strength (14.74MPa to 4.04MPa).In the morphological analysis,limited interaction between
fillers and matrices was clearly observed on the fracture
surfaces and manifested as voids,cracks,and particles
agglomeration also supported by compositional characteristics in term of their their bonding. |
---|