Removal Of Arsenic Using Synthetic Iron Oxyhydroxide
Removal of arsenic from mine waste water using iron-oxide-based absorbents are getting prevalent as using the absorbents are simpler and of low cost. In this research work, selected samples of synthetic iron oxyhydroxide powder were obtained. After characterization, these sample powders were used as...
保存先:
第一著者: | |
---|---|
フォーマット: | Monograph |
言語: | English |
出版事項: |
Universiti Sains Malaysia
2018
|
主題: | |
オンライン・アクセス: | http://eprints.usm.my/53241/1/Removal%20Of%20Arsenic%20Using%20Synthetic%20Iron%20Oxyhydroxide_Nur%20Aina%20Najeehah%20Mohd%20Aaznan_B1_2018.pdf http://eprints.usm.my/53241/ |
タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
id |
my.usm.eprints.53241 |
---|---|
record_format |
eprints |
spelling |
my.usm.eprints.53241 http://eprints.usm.my/53241/ Removal Of Arsenic Using Synthetic Iron Oxyhydroxide Mohd Aaznan, Nur Aina Najeehah T Technology TN Mining Engineering. Metallurgy Removal of arsenic from mine waste water using iron-oxide-based absorbents are getting prevalent as using the absorbents are simpler and of low cost. In this research work, selected samples of synthetic iron oxyhydroxide powder were obtained. After characterization, these sample powders were used as an absorbent in the arsenic removal experiment. The powdered samples were placed in separate 250 mL conical flask containing 100 mL of As (V) standard solution of varying concentrations (5, 7, and 9 ppm). The experiment was conducted for 8 hours with 20 mL volume of aliquot samples taken at 1, 3, 5, and 8 hours interval hour. The concentration of the As after the removal experiment in each aliquot sample was analysed using ICP-OES. The XRD pattern of the powdered samples obtained showed major characteristic peaks of goethite and hematite. Surface morphology of the powdered samples displayed dendritic features and were highly porous. These features were found to enhance the recovery of As from the standard solution prepared. The percentage of As removed at varying concentration of As was found to be in the range of 28.9% to 99.2%. The solid residues after the arsenic removal experiment were also characterised. From XRD phase analysis, the presence of arsenic oxide (As2O3) was detected. The surfaces of the solid residues were observed to be smoother and less dendritic from the SEM photomicrograph. It can be assumed that arsenic species were adsorbed into the pores on the surface of the synthetic iron oxyhydroxide powder samples after the arsenic removal experiment. Universiti Sains Malaysia 2018-06-13 Monograph NonPeerReviewed application/pdf en http://eprints.usm.my/53241/1/Removal%20Of%20Arsenic%20Using%20Synthetic%20Iron%20Oxyhydroxide_Nur%20Aina%20Najeehah%20Mohd%20Aaznan_B1_2018.pdf Mohd Aaznan, Nur Aina Najeehah (2018) Removal Of Arsenic Using Synthetic Iron Oxyhydroxide. Project Report. Universiti Sains Malaysia, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral. (Submitted) |
institution |
Universiti Sains Malaysia |
building |
Hamzah Sendut Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Sains Malaysia |
content_source |
USM Institutional Repository |
url_provider |
http://eprints.usm.my/ |
language |
English |
topic |
T Technology TN Mining Engineering. Metallurgy |
spellingShingle |
T Technology TN Mining Engineering. Metallurgy Mohd Aaznan, Nur Aina Najeehah Removal Of Arsenic Using Synthetic Iron Oxyhydroxide |
description |
Removal of arsenic from mine waste water using iron-oxide-based absorbents are getting prevalent as using the absorbents are simpler and of low cost. In this research work, selected samples of synthetic iron oxyhydroxide powder were obtained. After characterization, these sample powders were used as an absorbent in the arsenic removal experiment. The powdered samples were placed in separate 250 mL conical flask containing 100 mL of As (V) standard solution of varying concentrations (5, 7, and 9 ppm). The experiment was conducted for 8 hours with 20 mL volume of aliquot samples taken at 1, 3, 5, and 8 hours interval hour. The concentration of the As after the removal experiment in each
aliquot sample was analysed using ICP-OES. The XRD pattern of the powdered samples obtained showed major characteristic peaks of goethite and hematite. Surface morphology of
the powdered samples displayed dendritic features and were highly porous. These features were found to enhance the recovery of As from the standard solution prepared. The
percentage of As removed at varying concentration of As was found to be in the range of 28.9% to 99.2%. The solid residues after the arsenic removal experiment were also
characterised. From XRD phase analysis, the presence of arsenic oxide (As2O3) was detected. The surfaces of the solid residues were observed to be smoother and less dendritic from the SEM photomicrograph. It can be assumed that arsenic species were adsorbed into the pores on the surface of the synthetic iron oxyhydroxide powder samples after the arsenic removal experiment. |
format |
Monograph |
author |
Mohd Aaznan, Nur Aina Najeehah |
author_facet |
Mohd Aaznan, Nur Aina Najeehah |
author_sort |
Mohd Aaznan, Nur Aina Najeehah |
title |
Removal Of Arsenic Using Synthetic Iron Oxyhydroxide |
title_short |
Removal Of Arsenic Using Synthetic Iron Oxyhydroxide |
title_full |
Removal Of Arsenic Using Synthetic Iron Oxyhydroxide |
title_fullStr |
Removal Of Arsenic Using Synthetic Iron Oxyhydroxide |
title_full_unstemmed |
Removal Of Arsenic Using Synthetic Iron Oxyhydroxide |
title_sort |
removal of arsenic using synthetic iron oxyhydroxide |
publisher |
Universiti Sains Malaysia |
publishDate |
2018 |
url |
http://eprints.usm.my/53241/1/Removal%20Of%20Arsenic%20Using%20Synthetic%20Iron%20Oxyhydroxide_Nur%20Aina%20Najeehah%20Mohd%20Aaznan_B1_2018.pdf http://eprints.usm.my/53241/ |
_version_ |
1738511177749626880 |
score |
13.153044 |