Dependence of Adhesion Properties on Blend Ratio of Ethylene-Propylene-Diene Rubber/Standard Malaysian Rubber Blend Adhesive
Viscosity, tack and, peel and shear strengths of ethylene-propylene-diene rubber (EPDM)/standard Malaysian rubber (SMR L) blend adhesive were studied using various blend ratios of the two rubbers, ranging from 0 to 100% EPDM. Coumarone-indene resin, toluene, and poly(ethylene terephthalate) (PET)...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Publishing Corporation
2013
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/38620/1/Dependence_of_Adhesion_Properties_on_Blend_Ratio_of_Ethylene-Propylene-Diene.pdf http://eprints.usm.my/38620/ http://dx.doi.org/10.1155/2013/383276 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Viscosity, tack and, peel and shear strengths of ethylene-propylene-diene rubber (EPDM)/standard Malaysian rubber (SMR L)
blend adhesive were studied using various blend ratios of the two rubbers, ranging from 0 to 100% EPDM. Coumarone-indene
resin, toluene, and poly(ethylene terephthalate) (PET) were used as the tackifier, solvent, and coating substrate, respectively. The
tackifier content was fixed at 40 parts per hundred parts of rubber (phr). A SHEEN hand coater was used to coat the adhesive
on PET film at four coating thicknesses, that is, 30, 60, 90, and 120 |
|---|