Synthetic graphite production of oil palm trunk chip at various heating rate via pyrolisis process
Synthetic graphite was synthesized from oil palm trunk chip in controlled heating condition or pyrolysis process. The heating rate (5 °/min, 10 °/min and 20 °/min) were varied whilst the heating temperature at 800 °C was fixed. After heat treatment process, the samples were characterized by X-Ray Di...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2019
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/82358/1/Synthetic%20graphite%20production%20of%20oil%20palm%20trunk%20chip%20at%20various%20heating%20rate%20via%20pyrolisis%20process.pdf http://psasir.upm.edu.my/id/eprint/82358/ https://www.sciencedirect.com/science/article/pii/S2214785319314452 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Synthetic graphite was synthesized from oil palm trunk chip in controlled heating condition or pyrolysis process. The heating rate (5 °/min, 10 °/min and 20 °/min) were varied whilst the heating temperature at 800 °C was fixed. After heat treatment process, the samples were characterized by X-Ray Diffraction (XRD) and analyzed using X’Pert Highscore Plus software. Graphite phase was analysed by XRD and it was further supported by RAMAN spectroscopy analysis to confirm the graphitic nature of the synthetic graphite obtained. The morphological study was carried out by using Scanning Electron Microscope (SEM). Based on the analysis, it was confirm that synthetic graphite was successfully synthesized by heat treatment at 800 °C (20 °/min heating rate). Synthetic graphite were observed in the form of amorphous carbon based on the XRD diffraction pattern that match with the reference code of 00-041-1487. RAMAN spectroscopy also showed the formation on D, G and 2D peaks at the respective wavenumber of 1250 cm-1, 1625 cm-1 and 2700 cm-1. |
|---|