Effect of Co3O4 doping on nonlinear coefficient in Zn-Bi-Ti-O varistor ceramics
In the ZnO based varistor, the improvement of nonlinear coefficient (α) and prevention of evaporation of Bi2O3 during heat treatments can be achieved by the addition of MnO2 or Co3O4. In this conjunction, it is proper to see the effect of these additives at different low mol percentage and sintering...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Trans Tech Publications
2015
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/36966/1/Effect%20of%20Co3O4%20doping%20on%20nonlinear%20coefficient%20in%20Zn-Bi-Ti-O%20varistor%20ceramics.pdf http://psasir.upm.edu.my/id/eprint/36966/ http://www.scientific.net/AMR.1107.20 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In the ZnO based varistor, the improvement of nonlinear coefficient (α) and prevention of evaporation of Bi2O3 during heat treatments can be achieved by the addition of MnO2 or Co3O4. In this conjunction, it is proper to see the effect of these additives at different low mol percentage and sintering conditions to nonlinear coefficient improvement of the varistor ceramics. In this paper, the investigation regarding to the α variation of Co3O4 doping on ZnO-Bi2O3-TiO2 system is discussed. Here, the crystalline phases were identified by an XRD (PANalytical (Philips) XPert Pro PW3040/60) with CuKα radiation and the data were analyzed by using XPert High Score software. The density of varistor ceramics was measured by the geometrical method. The current-voltage characteristics of the varistor ceramics were evaluated. The average grain size (d) was determined by lineal intercept method. The α of ZnO doped with 0.5 mol% of Bi2O3, 0.5 mol% of TiO2 and x mol% of Co3O4 was calculated from data analysis of current-voltage characteristics obtained through a Source Measure Unit (Keithley 236). The calculation of α is done by using Origin Pro8.0 software. The value of α at low concentration at 1170 °C has the value 5.36 and 3 at 45 and 90 min sintering time, respectively, and then decreases to 4.99 and 2.98 at 0.8 mol% Co3O4 concentrations. When the amount of dopant is increased then the value of α increase up to 0.4 mol% and then the value are slightly dropped after further addition. The addition of Co3O4 dopant in Zn-Bi-Ti oxide ceramics sintered at 45 minutes cause the value of α to increase up to 0.4 mol% and decrease after further addition. |
|---|