AC Susceptibility and Electrical Properties of BiFeO3 Nanoparticles Added Bi1.6Pb0.4Sr2Ca2Cu3O10 Superconductor

• المؤلفون الرئيسيون: Suib N.R.M., Ilhamsyah A.B.P., Mujaini M., Mahat A.M., Abd-Shukor R.
• مؤلفون آخرون: 24072061100
• التنسيق: مقال
• منشور في: Springer 2024
• الموضوعات: Flux pinning center; Superparamagnetism; Transport current density; Barium compounds; Calcium compounds; Chromium compounds; Cobalt compounds; Copper compounds; Critical currents; Current density; Flux pinning; II-VI semiconductors; Iron compounds; Magnesia; Magnetic susceptibility; Nanomagnetics; Nanoparticles; Nickel compounds; Precipitation (chemical); Strontium compounds; Superconducting transition temperature; Textures; Zinc oxide; A.C. susceptibility; Bi-2223; Bi-2223 superconductors; Bismuth ferrites; Coprecipitation method; Flux pinning centers; Temperature dependent; Transport critical current density; Transport currents; Bismuth compounds

The effect of bismuth ferrite (BiFeO3) nanoparticles (~ 20�nm) on Bi1.6Pb0.4Sr2Ca2Cu3O10 (Bi-2223) superconductor was studied. Bi-2223 powders with starting formula Bi1.6Pb0.4Sr2Ca2Cu3O10(BiFeO3)x for x = 0�0.20 wt.% were prepared using the co-precipitation method. The temperature dependent electric...