Aspects of wear mechanisms of carbide tools when machine Hastelloy C-22HS

• Main Authors: Kadirgama K., Noor M.M., Abou-El-Hossein K.A., Mohammad B., Habeeb H.H.
• 其他作者: 12761486500
• 格式: Conference Paper
• 出版: 2023
• 主題: Carbide inserts; Nickel superalloys; Tool wear; Carbide tools; Cracking (chemical); Cutting tools; Hydraulic structures; Machine tools; Metal working tools; Nickel alloys; Scanning electron microscopy; Superalloys; Tribology; Wear of materials; Crater wear; Fast rate; Hastelloy; High temperature; Intergranular fracture; Microstructure defects; Nickel superalloy; SEM; Thermal cracking; Wear mechanisms; Carbides

In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/TiN experienced severe intergra...