Effect of the grain size of nanoparticle dye-coated titanium dioxide on the short-circuit current density and open-circuit voltage of an indium tin oxide/titanium dioxide/poly(acrylonitrile)-propylene carbonate-lithium perchlorate/graphite solar cell

• 主要な著者: Rika, Rahman M.Y.A., Salleh M.M., Umar A.A., Ahmad A.
• その他の著者: 36009299200
• フォーマット: 論文
• 出版事項: 2023
• 主題: Coatings; Conducting polymers; Dyes/pigments; Electrochemistry; Photophysics; Film preparation; Grain size and shape; Graphite; Graphite electrodes; Indium; Lithium; Open circuit voltage; Organic conductors; Plastic coatings; Plasticizers; Propylene; Scanning electron microscopy; Solar cells; Spin glass; Substrates; Switching circuits; Tin; Tin dioxide; Titanium; Titanium castings; Titanium dioxide; Titanium oxides; Average grain size; Coated titanium; Controlled hydrolysis; Dye sensitized; Electron beam evaporation; Glass slides; Glass substrates; Grain size; Indium tin oxide; Lithium perchlorate; Methyl Red dye; Propylene carbonate; Rectification properties; Solution-casting technique; TiO; coating; electrochemistry; electrolyte; film; hydrolysis; particle size; titanium dioxide; ITO glass

A dye-sensitized indium tin oxide (ITO)/titanium dioxide (TiO 2)/polyacrylonitrile (PAN)-propylene carbonate (PC)-lithium perchlorate (LiClO4)/graphite solar cell was fabricated, and its performance was tested in the dark and under the illumination of a 100 mW/cm2 light. Three TiO2 samples were used...