Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM)
One major problem that storming the manufacturing industry is the poor life cycle of the manufactured steel product where it does not last long when there is an external force is applied. It is always known that surface finishing treatment improves the life cycle of a metal steel.
Saved in:
Main Author: | |
---|---|
Format: | text::Final Year Project |
Language: | English US |
Published: |
2023
|
Subjects: | |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.uniten.dspace-28013 |
---|---|
record_format |
dspace |
spelling |
my.uniten.dspace-280132023-09-10T02:03:58Z Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) Vignesh Rao A/L Sanny Bavu Metals - Finishing Sand-blast One major problem that storming the manufacturing industry is the poor life cycle of the manufactured steel product where it does not last long when there is an external force is applied. It is always known that surface finishing treatment improves the life cycle of a metal steel. 2023-09-06T03:18:55Z 2023-09-06T03:18:55Z 2017 Resource Types::text::Final Year Project https://irepository.uniten.edu.my/handle/123456789/28013 en_US application/pdf |
institution |
Universiti Tenaga Nasional |
building |
UNITEN Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Tenaga Nasional |
content_source |
UNITEN Institutional Repository |
url_provider |
http://dspace.uniten.edu.my/ |
language |
English US |
topic |
Metals - Finishing Sand-blast |
spellingShingle |
Metals - Finishing Sand-blast Vignesh Rao A/L Sanny Bavu Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) |
description |
One major problem that storming the manufacturing industry is the poor life cycle of the manufactured steel product where it does not last long when there is an external force is applied. It is always known that surface finishing treatment improves the life cycle of a metal steel. |
format |
Resource Types::text::Final Year Project |
author |
Vignesh Rao A/L Sanny Bavu |
author_facet |
Vignesh Rao A/L Sanny Bavu |
author_sort |
Vignesh Rao A/L Sanny Bavu |
title |
Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) |
title_short |
Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) |
title_full |
Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) |
title_fullStr |
Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) |
title_full_unstemmed |
Study of fatique life of astm A516 grade 70 steel after sandblasting with grade SAE-G 80 (0.3 MM) |
title_sort |
study of fatique life of astm a516 grade 70 steel after sandblasting with grade sae-g 80 (0.3 mm) |
publishDate |
2023 |
_version_ |
1806426570699571200 |
score |
13.19449 |