Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications

This research work focuses on the mechanical properties and microstructural behavior of high-purity CeO2 and MnO2-doped Y-TZP. The compositions were varied with different weight percentage i.e from 0.5 to 1.5wt%. The samples were homogenously mixed using wet milling and ball milling operations. Then...

全面介绍

Saved in:
书目详细资料
Main Authors: Sankar G., Meenaloshini S., Dinesh R.
其他作者: 57209466755
格式: Article
出版: Blue Eyes Intelligence Engineering and Sciences Publication 2023
标签: 添加标签
没有标签, 成为第一个标记此记录!
id my.uniten.dspace-24675
record_format dspace
spelling my.uniten.dspace-246752023-05-29T15:25:45Z Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications Sankar G. Meenaloshini S. Dinesh R. 57209466755 48561725600 56740614600 This research work focuses on the mechanical properties and microstructural behavior of high-purity CeO2 and MnO2-doped Y-TZP. The compositions were varied with different weight percentage i.e from 0.5 to 1.5wt%. The samples were homogenously mixed using wet milling and ball milling operations. Then, the samples were shaped into circular discs and rectangular bars by uniaxial pressing at 200 MPa and then pressure less-sintered at various temperatures between 1250?C and 1450?C. 1h holding time was applied before cooling down. The results have shown, that the addition of dopant and sintering temperature has significantly contributed towards the enhancement of the mechanical properties of Y-TZP. The mechanical properties in relation to bulk density, Young�s modulus, Vickers hardness, and flexural were measured. The best mechanical property values for the CeO2 and MnO2-doped Y-TZP ceramics were 5.67 Mgm-3 and 8.46 GPa for density and Vickers hardness, respectively. The best flexural strength and Youngs modulus values obtained from the experiment were ~900 MPa and 210 GPa respectively. These results indicate that the addition of dopants have reinforced the densification parameters and toughened the samples. These results were obtained for the composition of 0.5wt% MnO2 and 0.5wt% CeO2 sintered at 1350?C. � BEIESP. Final 2023-05-29T07:25:45Z 2023-05-29T07:25:45Z 2019 Article 2-s2.0-85067872719 https://www.scopus.com/inward/record.uri?eid=2-s2.0-85067872719&partnerID=40&md5=6368f60519712825c25212e0333b210e https://irepository.uniten.edu.my/handle/123456789/24675 8 7 337 341 Blue Eyes Intelligence Engineering and Sciences Publication Scopus
institution Universiti Tenaga Nasional
building UNITEN Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Tenaga Nasional
content_source UNITEN Institutional Repository
url_provider http://dspace.uniten.edu.my/
description This research work focuses on the mechanical properties and microstructural behavior of high-purity CeO2 and MnO2-doped Y-TZP. The compositions were varied with different weight percentage i.e from 0.5 to 1.5wt%. The samples were homogenously mixed using wet milling and ball milling operations. Then, the samples were shaped into circular discs and rectangular bars by uniaxial pressing at 200 MPa and then pressure less-sintered at various temperatures between 1250?C and 1450?C. 1h holding time was applied before cooling down. The results have shown, that the addition of dopant and sintering temperature has significantly contributed towards the enhancement of the mechanical properties of Y-TZP. The mechanical properties in relation to bulk density, Young�s modulus, Vickers hardness, and flexural were measured. The best mechanical property values for the CeO2 and MnO2-doped Y-TZP ceramics were 5.67 Mgm-3 and 8.46 GPa for density and Vickers hardness, respectively. The best flexural strength and Youngs modulus values obtained from the experiment were ~900 MPa and 210 GPa respectively. These results indicate that the addition of dopants have reinforced the densification parameters and toughened the samples. These results were obtained for the composition of 0.5wt% MnO2 and 0.5wt% CeO2 sintered at 1350?C. � BEIESP.
author2 57209466755
author_facet 57209466755
Sankar G.
Meenaloshini S.
Dinesh R.
format Article
author Sankar G.
Meenaloshini S.
Dinesh R.
spellingShingle Sankar G.
Meenaloshini S.
Dinesh R.
Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications
author_sort Sankar G.
title Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications
title_short Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications
title_full Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications
title_fullStr Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications
title_full_unstemmed Densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal Zirconia polycrystals ceramics for dental applications
title_sort densification behavior and mechanical properties of cerium oxide and manganese oxide-doped yttria tetragonal zirconia polycrystals ceramics for dental applications
publisher Blue Eyes Intelligence Engineering and Sciences Publication
publishDate 2023
_version_ 1806425700509417472
score 13.250246