To study the fatigue crack growth in welded steel
This study investigates fatigue crack growth of two type welding subjected HAZ (Heat Affected Zone), Porosity, Slag Inclusion. Metal weld were produced in 5mm thick A516 GRADE 70 plates with a single "V" without post-weld treatment. A Tensile test was used to both type of welding. Liquid P...
Saved in:
| Main Author: | |
|---|---|
| Format: | text::Thesis |
| Language: | English |
| Published: |
2023
|
| Subjects: | |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| id |
my.uniten.dspace-20948 |
|---|---|
| record_format |
dspace |
| spelling |
my.uniten.dspace-209482023-05-04T13:23:58Z To study the fatigue crack growth in welded steel Thines Murugan Materials -- Fatigue Steel -- Fatigue Steel fracture This study investigates fatigue crack growth of two type welding subjected HAZ (Heat Affected Zone), Porosity, Slag Inclusion. Metal weld were produced in 5mm thick A516 GRADE 70 plates with a single "V" without post-weld treatment. A Tensile test was used to both type of welding. Liquid Penetrant test were conducted under room temperature to identify crack within the welding joint of SMAW and MIG. Microstructure Testing were used under magnification of 500x to identify the fatigue crack growth. Radiographic film test were conducted in X-rays emission to identify inner crack growth and type of growth within SMAW and MIG type of welding. 2023-05-03T15:37:59Z 2023-05-03T15:37:59Z 2015 Resource Types::text::Thesis https://irepository.uniten.edu.my/handle/123456789/20948 en application/pdf |
| institution |
Universiti Tenaga Nasional |
| building |
UNITEN Library |
| collection |
Institutional Repository |
| continent |
Asia |
| country |
Malaysia |
| content_provider |
Universiti Tenaga Nasional |
| content_source |
UNITEN Institutional Repository |
| url_provider |
http://dspace.uniten.edu.my/ |
| language |
English |
| topic |
Materials -- Fatigue Steel -- Fatigue Steel fracture |
| spellingShingle |
Materials -- Fatigue Steel -- Fatigue Steel fracture Thines Murugan To study the fatigue crack growth in welded steel |
| description |
This study investigates fatigue crack growth of two type welding subjected HAZ (Heat Affected Zone), Porosity, Slag Inclusion. Metal weld were produced in 5mm thick A516 GRADE 70 plates with a single "V" without post-weld treatment. A Tensile test was used to both type of welding. Liquid Penetrant test were conducted under room temperature to identify crack within the welding joint of SMAW and MIG. Microstructure Testing were used under magnification of 500x to identify the fatigue crack growth. Radiographic film test were conducted in X-rays emission to identify inner crack growth and type of growth within SMAW and MIG type of welding. |
| format |
Resource Types::text::Thesis |
| author |
Thines Murugan |
| author_facet |
Thines Murugan |
| author_sort |
Thines Murugan |
| title |
To study the fatigue crack growth in welded steel |
| title_short |
To study the fatigue crack growth in welded steel |
| title_full |
To study the fatigue crack growth in welded steel |
| title_fullStr |
To study the fatigue crack growth in welded steel |
| title_full_unstemmed |
To study the fatigue crack growth in welded steel |
| title_sort |
to study the fatigue crack growth in welded steel |
| publishDate |
2023 |
| _version_ |
1806423521098727424 |
| score |
13.214268 |