An investigation on titanium doping in reduced graphene oxide by RF magnetron sputtering for dye-sensitized solar cells
A study investigating the effects of titanium (Ti)atoms sputtered from different sources on substrate distance was attempted in order to effectively dope a reduced graphene oxide (rGO)thin film surface. Factors such as crystallinity, morphology, phase formation, light absorption, and surface chemica...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2020
|
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | A study investigating the effects of titanium (Ti)atoms sputtered from different sources on substrate distance was attempted in order to effectively dope a reduced graphene oxide (rGO)thin film surface. Factors such as crystallinity, morphology, phase formation, light absorption, and surface chemical state of rGO-TiO2 were investigated. As a result, functional groups or chemical states revealed the presence of Ti-O-C in rGO-TiO2 nanocomposite after the sputtering process. The titanium source from the target was of Ti3+ species as determined using X-ray photoelectron spectroscopy (XPS). It was found that average sized Ti3+ ions of around 59.4 nm were incorporated into the rGO nanosheet. A customized Dye-Sensitized Solar Cells (DSSCs)device was fabricated with the photo-anode consisting of sputtered rGO-TiO2 nanocomposite. After optimization, the Ti target allocated with 10 cm-apart FTO glass-coated rGO nanosheet and 0.67 cm2 active area exhibited an ideal PCE of 6.60%, which is remarkably higher than the usual 5 cm sputtering distance the sample (1.90%)had achieved. © 2019 |
|---|