The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets

Link to publisher's homepage at http://www.um.edu.my/

Saved in:
Bibliographic Details
Main Authors: Shamsul Baharin, Jamaludin, Prof. Dr., Ahmad Latiffi, A. A. T., Khairel Rafezi, Ahmad, Md. Fazlul, Bari
Format: Article
Language:English
Published: University of Malaya 2010
Subjects:
Microstructural
Mild steel
Spot welding
Tensile shear test
Corrosive
Online Access:http://dspace.unimap.edu.my/xmlui/handle/123456789/9035
Tags: Add Tag
No Tags, Be the first to tag this record!
id my.unimap-9035
record_format dspace
spelling my.unimap-90352010-08-24T04:33:37Z The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets Shamsul Baharin, Jamaludin, Prof. Dr. Ahmad Latiffi, A. A. T. Khairel Rafezi, Ahmad Md. Fazlul, Bari Microstructural Mild steel Spot welding Tensile shear test Corrosive Link to publisher's homepage at http://www.um.edu.my/ In the present work, mild steel sheets consisting two batches were welded by resistance spot welding at different welding parameters and exposed under different environments. The 5% sodium chloride brine was used in the salt spray test, produced a whole rusty surface on the tested specimens (batch 2). The welding joints were subjected to tensile-shearing test in order to determine the strength of the welded joints from ambient and in corrosive environment. Tensile-shear test showed significant differences on the failure load between these two batches where corrosion had affected the surface strength of the welded steel. The results also showed that the highest tensile shear strength is given by the specimen welded using 4kA current at 4 cycles. 2010-08-24T04:33:37Z 2010-08-24T04:33:37Z 2009 Article International Journal of Mechanical and Materials Engineering, vol. 4(2), 2009, pages 208-210 1823-0334 ejum.fsktm.um.edu.my/VolumeListing.aspx?JournalID=19 http://hdl.handle.net/123456789/9035 en University of Malaya
institution Universiti Malaysia Perlis
building UniMAP Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Malaysia Perlis
content_source UniMAP Library Digital Repository
url_provider http://dspace.unimap.edu.my/
language English
topic Microstructural
Mild steel
Spot welding
Tensile shear test
Corrosive
spellingShingle Microstructural
Mild steel
Spot welding
Tensile shear test
Corrosive
Shamsul Baharin, Jamaludin, Prof. Dr.
Ahmad Latiffi, A. A. T.
Khairel Rafezi, Ahmad
Md. Fazlul, Bari
The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
description Link to publisher's homepage at http://www.um.edu.my/
format Article
author Shamsul Baharin, Jamaludin, Prof. Dr.
Ahmad Latiffi, A. A. T.
Khairel Rafezi, Ahmad
Md. Fazlul, Bari
author_facet Shamsul Baharin, Jamaludin, Prof. Dr.
Ahmad Latiffi, A. A. T.
Khairel Rafezi, Ahmad
Md. Fazlul, Bari
author_sort Shamsul Baharin, Jamaludin, Prof. Dr.
title The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
title_short The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
title_full The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
title_fullStr The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
title_full_unstemmed The influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
title_sort influence of welding parameters and corrosive environment on the joint strength of resistance spot-welded mild steel sheets
publisher University of Malaya
publishDate 2010
url http://dspace.unimap.edu.my/xmlui/handle/123456789/9035
_version_ 1643789219822305280
score 13.222552

Similar Items