Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater

The corrosion behavior of 8.6 Al-Cu alloy was investigated in 4 different conditions of South China Seawater. The weight loss curve of alloy increases with time during the initial exposure period, due to dissolution of deposit. The films formed were thick, porous and adhered on the surface of the al...

Full description

Saved in:
Bibliographic Details
Main Authors: Mohammed Misbahul, Amin, Seoh Soo Yee, W. B., Wan Nik
Format: Article
Language:English
Published: Sadguru Publications 2009
Subjects:
8.6 A1-Cu alloy
South China Seawater
Scale morphologies
Alloys
Oxidation
Marine corrosion
Corrosion
Online Access:http://dspace.unimap.edu.my/xmlui/handle/123456789/6177
Tags: Add Tag
No Tags, Be the first to tag this record!
id my.unimap-6177
record_format dspace
spelling my.unimap-61772009-06-19T09:25:59Z Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater Mohammed Misbahul, Amin Seoh Soo Yee W. B., Wan Nik 8.6 A1-Cu alloy South China Seawater Scale morphologies Alloys Oxidation Marine corrosion Corrosion The corrosion behavior of 8.6 Al-Cu alloy was investigated in 4 different conditions of South China Seawater. The weight loss curve of alloy increases with time during the initial exposure period, due to dissolution of deposit. The films formed were thick, porous and adhered on the surface of the alloy. The seawater species have deleterious effect on the protectively of the surface and rapid degradation of the alloy is noted. The morphologies of deposits on the surface of alloy were determined by using polarized microscope. 2009-06-19T09:25:58Z 2009-06-19T09:25:58Z 2005 Article 0972-768X http://hdl.handle.net/123456789/6177 en Sadguru Publications Faculty of Science and Technology, University College of Science and Technology Malaysia
institution Universiti Malaysia Perlis
building UniMAP Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Malaysia Perlis
content_source UniMAP Library Digital Repository
url_provider http://dspace.unimap.edu.my/
language English
topic 8.6 A1-Cu alloy
South China Seawater
Scale morphologies
Alloys
Oxidation
Marine corrosion
Corrosion
spellingShingle 8.6 A1-Cu alloy
South China Seawater
Scale morphologies
Alloys
Oxidation
Marine corrosion
Corrosion
Mohammed Misbahul, Amin
Seoh Soo Yee
W. B., Wan Nik
Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
description The corrosion behavior of 8.6 Al-Cu alloy was investigated in 4 different conditions of South China Seawater. The weight loss curve of alloy increases with time during the initial exposure period, due to dissolution of deposit. The films formed were thick, porous and adhered on the surface of the alloy. The seawater species have deleterious effect on the protectively of the surface and rapid degradation of the alloy is noted. The morphologies of deposits on the surface of alloy were determined by using polarized microscope.
format Article
author Mohammed Misbahul, Amin
Seoh Soo Yee
W. B., Wan Nik
author_facet Mohammed Misbahul, Amin
Seoh Soo Yee
W. B., Wan Nik
author_sort Mohammed Misbahul, Amin
title Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
title_short Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
title_full Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
title_fullStr Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
title_full_unstemmed Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
title_sort oxidation behaviour of 8.6 al-cu alloy in south china seawater
publisher Sadguru Publications
publishDate 2009
url http://dspace.unimap.edu.my/xmlui/handle/123456789/6177
_version_ 1643788465138040832
score 13.23648

Similar Items