Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10
In this study, ETS-10 precursors were mixed with graphene oxide (GO) suspension to obtain GO incorporated ETS-10 (GO/ETS-10) with improved adsorption ability and photocatalytic activity in comparison to that of ETS-10. The GO/ETS-10 composite prepared with different GO to ETS-10 ratios, i.e. 1:15, 1...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English English |
Published: |
2017
|
Subjects: | |
Online Access: | https://eprints.ums.edu.my/id/eprint/38962/1/24%20PAGES.pdf https://eprints.ums.edu.my/id/eprint/38962/2/FULLTEXT.pdf https://eprints.ums.edu.my/id/eprint/38962/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my.ums.eprints.38962 |
---|---|
record_format |
eprints |
spelling |
my.ums.eprints.389622024-06-27T07:42:06Z https://eprints.ums.edu.my/id/eprint/38962/ Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 Nguang, Sing Yew QD701-731 Photochemistry In this study, ETS-10 precursors were mixed with graphene oxide (GO) suspension to obtain GO incorporated ETS-10 (GO/ETS-10) with improved adsorption ability and photocatalytic activity in comparison to that of ETS-10. The GO/ETS-10 composite prepared with different GO to ETS-10 ratios, i.e. 1:15, 1:10 and 1:5 were confirmed by XRD, FTIR, EDX and XPS analyses. The results showed that GO and ETS-10 were chemically bound through Ti–O–C and Si–O–C bonding. SEM images showed that the truncated bipyramidal ETS-10 crystals were grown firmly on the GO surface and have crystal sizes range between 0.5 to 1.0 μm. Thermogravimetric analysis revealed that the synthesized GO/ETS-10 composite was thermally stable up to 150 ˚C and decomposed fully above 400 ˚C due to the disintegration of GO from ETS-10. The band gap energy for GO/ETS-10(1:5) was determined to be 3.12 eV which was lower than ETS-10 (3.48 eV). The adsorption study revealed that the adsorption behavior of MB onto GO/ETS-10 was mainly monolayer due to the chemisorption interaction between MB and GO/ETS-10 surface. The maximum equilibrium adsorption capacity of GO/ETS-10 was calculated to be 294 mg/g, which is much higher than ETS-10 with only 139 mg/g. Besides that, GO/ETS-10 can be photoexcited by both UV-A and visible radiations which gave similar removal of MB in water. This implies that the presence of GO can help to widen the light responsive range of ETS-10 by lowering the band gap energy and suppress the electron-hole recombination. 0.075 g/L of GO/ETS-10(1:5) in 20-ppm MB solution with UV-A irradiation (as GO/ETS-10(1:5)/UV-A), for instance, can achieve about 65 % of MB removal after 6 hours and still increasing with a consistent rate of removal in comparison to 60 % of MB removal achieved by GO/ETS-10(1:5)/Dark system, which has reached plateau after 6 hours of reaction. The results showed that the photocatalytic activity of GO/ETS-10 was low under UV-A irradiation but it is important to ensure continuous adsorption-photocatalytic removal throughout the process. Besides, it was found that addition of 5 x 10-3 mol/L H2O2 in the photocatalytic system (as GO/ETS-10(1:5)/H2O2/UV-A system) was capable to enhance about 20 % of MB removal, which giving a total of 93 % after 8 hours. This study implies that GO/ETS-10 composite can be a potential material specifically for the elimination of organic pollutant via adsorption and eventually through photocatalytic decomposition under sunlight. 2017 Thesis NonPeerReviewed text en https://eprints.ums.edu.my/id/eprint/38962/1/24%20PAGES.pdf text en https://eprints.ums.edu.my/id/eprint/38962/2/FULLTEXT.pdf Nguang, Sing Yew (2017) Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10. Masters thesis, Universiti Malaysia Sabah. |
institution |
Universiti Malaysia Sabah |
building |
UMS Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Malaysia Sabah |
content_source |
UMS Institutional Repository |
url_provider |
http://eprints.ums.edu.my/ |
language |
English English |
topic |
QD701-731 Photochemistry |
spellingShingle |
QD701-731 Photochemistry Nguang, Sing Yew Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
description |
In this study, ETS-10 precursors were mixed with graphene oxide (GO) suspension to obtain GO incorporated ETS-10 (GO/ETS-10) with improved adsorption ability and photocatalytic activity in comparison to that of ETS-10. The GO/ETS-10 composite prepared with different GO to ETS-10 ratios, i.e. 1:15, 1:10 and 1:5 were confirmed by XRD, FTIR, EDX and XPS analyses. The results showed that GO and ETS-10 were chemically bound through Ti–O–C and Si–O–C bonding. SEM images showed that the truncated bipyramidal ETS-10 crystals were grown firmly on the GO surface and have crystal sizes range between 0.5 to 1.0 μm. Thermogravimetric analysis revealed that the synthesized GO/ETS-10 composite was thermally stable up to 150 ˚C and decomposed fully above 400 ˚C due to the disintegration of GO from ETS-10. The band gap energy for GO/ETS-10(1:5) was determined to be 3.12 eV which was lower than ETS-10 (3.48 eV). The adsorption study revealed that the adsorption behavior of MB onto GO/ETS-10 was mainly monolayer due to the chemisorption interaction between MB and GO/ETS-10 surface. The maximum equilibrium adsorption capacity of GO/ETS-10 was calculated to be 294 mg/g, which is much higher than ETS-10 with only 139 mg/g. Besides that, GO/ETS-10 can be photoexcited by both UV-A and visible radiations which gave similar removal of MB in water. This implies that the presence of GO can help to widen the light responsive range of ETS-10 by lowering the band gap energy and suppress the electron-hole recombination. 0.075 g/L of GO/ETS-10(1:5) in 20-ppm MB solution with UV-A irradiation (as GO/ETS-10(1:5)/UV-A), for instance, can achieve about 65 % of MB removal after 6 hours and still increasing with a consistent rate of removal in comparison to 60 % of MB removal achieved by GO/ETS-10(1:5)/Dark system, which has reached plateau after 6 hours of reaction. The results showed that the photocatalytic activity of GO/ETS-10 was low under UV-A irradiation but it is important to ensure continuous adsorption-photocatalytic removal throughout the process. Besides, it was found that addition of 5 x 10-3 mol/L H2O2 in the photocatalytic system (as GO/ETS-10(1:5)/H2O2/UV-A system) was capable to enhance about 20 % of MB removal, which giving a total of 93 % after 8 hours. This study implies that GO/ETS-10 composite can be a potential material specifically for the elimination of organic pollutant via adsorption and eventually through photocatalytic decomposition under sunlight. |
format |
Thesis |
author |
Nguang, Sing Yew |
author_facet |
Nguang, Sing Yew |
author_sort |
Nguang, Sing Yew |
title |
Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
title_short |
Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
title_full |
Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
title_fullStr |
Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
title_full_unstemmed |
Adsorption and photocatalytic removal of Methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
title_sort |
adsorption and photocatalytic removal of methylene blue using graphene oxide-supported engelhard titanosilicate-10 |
publishDate |
2017 |
url |
https://eprints.ums.edu.my/id/eprint/38962/1/24%20PAGES.pdf https://eprints.ums.edu.my/id/eprint/38962/2/FULLTEXT.pdf https://eprints.ums.edu.my/id/eprint/38962/ |
_version_ |
1803335891803963392 |
score |
13.18916 |