Influence of Anodizing Parameters on the Morphological Characteristics of TNTAs

• Main Authors: Aamina, Aamina, Hossen, Md. Arif, Azrina, Abd Aziz
• Format: Article
• Language: English
• Published: Penerbit UMP 2023
• Subjects: TA Engineering (General). Civil engineering (General)
• Online Access: http://umpir.ump.edu.my/id/eprint/39885/1/Influence%20of%20Anodizing%20Parameters%20on%20the%20Morphological%20Characteristics%20of%20TNTAs.pdf; http://umpir.ump.edu.my/id/eprint/39885/; https://journal.ump.edu.my/construction/article/view/9773/3070

TiO2nanotubes arrays (TNTAs) were synthesized using the anodization method in ethylene glycol (EG)-based electrolyte with different percentages of ammonium fluoride (0.3, 0.4, and 0.5 wt.%) and water content (2.5, 5, and 7.5% vol%). All the samples were ultrasonically cleaned in acetone, ethanol, and deionized water, then dried in air and kept in an etching solution for a while before anodization. The two-step anodization was carried out, followed by thermal treatment at 450°C for the crystallization. The nanotube samples were characterized using FE-SEM analysis. The FE-SEM results showed that the largest tube diameter was 87.74±1.89 nm of the TNTAs prepared in the EG electrolyte with a composition of 7.5% water content and 0.5% ammonium fluoride. The longest tube length analyzed was around 5.3 μm of the TNTAs prepared in the ethylene glycol electrolyte with the composition of 2.5% water content and 0.4% ammonium fluoride percentage, exhibiting a highly ordered, compact honeycomb structure and thick single-walled structure.