Investigating the Degradation Resistance Improvement of Polymer Surfactant Complex Drag Reducing Agent
Polymers-Surfactant complex efficacy in reducing the drag is of an interest subject in drag reduction research. Turbulent drag reduction (DR) efficiency of Sodium Polystyrene Sulfonate (NaPSS) sodium Alkylbenzene sulfonate complex was studied in a rotating disk apparatus. The solution complex was pr...
Saved in:
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Trans Tech Publications, Switzerland
2015
|
Subjects: | |
Online Access: | http://umpir.ump.edu.my/id/eprint/12804/1/Investigating%20the%20Degradation%20Resistance%20Improvement%20of%20Polymer%20Surfactant%20Complex%20Drag%20Reducing%20Agent.pdf http://umpir.ump.edu.my/id/eprint/12804/ https://doi.org/10.4028/www.scientific.net/AMM.789-790.7 https://doi.org/10.4028/www.scientific.net/AMM.789-790.7 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Polymers-Surfactant complex efficacy in reducing the drag is of an interest subject in drag reduction research. Turbulent drag reduction (DR) efficiency of Sodium Polystyrene Sulfonate (NaPSS) sodium Alkylbenzene sulfonate complex was studied in a rotating disk apparatus. The solution complex was prepared by varying the concentration of the polymer between 100 to 1200 ppm and the surfactant between 100 to 700ppm. Measurement of torque values were recorded for each sample. The NaPSS (Sodium Polystyrene Sulfante) was found to have an ability to reduce the drag in the turbulent flow. A significant improvement was recorded for the addition of tiny amount of surfactant to the polymer system compare to the pure polymer drag reduction. At high surfactant concentration, it was found that the polymer drag ability decrease. The polymer was degraded when it is subjected to a high shear stress. The degredation resistance was increased by the addation of the surfactant to the polymer solution at concentration range of 100ppm to 400ppm of surfactant |
---|