Enhanced Capacitance of a Nitrogen-containing Carbon-based Nanocomposite via Noncovalent Functionalization Method

Ordered carbon (OC) with large surface area was prepared via replication by using Santa Barbara Amorphous-15 as a template and sucrose as a carbon precursor. The prepared OC was then noncovalently functionalized with Basic Red 2 dye precursor (BR2) to obtain OC–BR2, a nitrogen-containing carbon-base...

Full description

Saved in:
Bibliographic Details
Main Authors: Nur Izzatie Hannah, Razman, Salasiah, Endud, Zainab, Ramli, Hendrik, Oktendy Lintang, Izan Izwan, Misnon, Hanapi, Mat
Format: Article
Language:English
Published: Elsevier 2015
Subjects:
Online Access:http://umpir.ump.edu.my/id/eprint/10496/1/Enhanced%20Capacitance%20of%20A%20Nitrogen-Containing%20Carbon-Based%20Nanocomposite%20Via%20Noncovalent%20Functionalization%20Method.pdf
http://umpir.ump.edu.my/id/eprint/10496/
http://dx.doi.org/10.1016/j.jiec.2015.07.008
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Ordered carbon (OC) with large surface area was prepared via replication by using Santa Barbara Amorphous-15 as a template and sucrose as a carbon precursor. The prepared OC was then noncovalently functionalized with Basic Red 2 dye precursor (BR2) to obtain OC–BR2, a nitrogen-containing carbon-based nanocomposite with enhanced electrical properties. The functionalization was explained through adsorption isotherm, kinetic, and thermodynamic studies performed under variable conditions. The electrochemical performance test results demonstrated that the nanocomposite presents enhanced capacitance (48.4%) compared with the original OC, with maximum specific capacitance of 227 F g−1 at 0.5 A g−1 in 1 M KOH electrolyte.