Organic-inorganic composite nanocoatings with superhydrophobicity and thermal stability
Purpose: This paper aims to investigate the thermal stability and hydrophobicity of difference alkyl chain of silanes with silicon (Si) micro- and nanoparticles. Design/methodology/approach: Sol-gel methods have been used to design superhydrophobic glass substrates through surface modification by us...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Published: |
Emerald Publishing
2024
|
| Subjects: | |
| Online Access: | http://eprints.um.edu.my/44945/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Purpose: This paper aims to investigate the thermal stability and hydrophobicity of difference alkyl chain of silanes with silicon (Si) micro- and nanoparticles. Design/methodology/approach: Sol-gel methods have been used to design superhydrophobic glass substrates through surface modification by using low-surface-energy Isooctyl trimethoxysilane (ITMS) and Ethyl trimethoxysilane (ETMS) solution. Hierarchical double-rough scale solid surface was built by Si micro- and nanoparticles to enhance the surface roughness. The prepared sol was applied onto glass substrate using dip-coating method and was dried at control temperature of 400°C inside the tube furnace. Findings: The glass substrate achieved the water contact angle as high as 154 ± 2° and 150.4 ± 2° for Si/ITMS and Si/ETMS films, respectively. The Si/ITMS and Si/ETMS also were equipped with low sliding angle as low as 3° and 5°, respectively. The Si micro- and nanoparticles in the coating system have created nanopillars between them, which will suspend the water droplets. Both superhydrophobic coatings have showed good stability against high temperature up to 200°C as there are no changes in WCA shown by both coatings. Si/ITMS film sustains its superhydrophobicity after impacting with further temperature up to 400°C and turns hydrophobic state at 450°C. Research limitations/implications: Findings will be useful to develop superhydrophobic coatings with high thermal stability. Practical implications: Sol method provides a suitable medium for the combination of organic-inorganic network to achieve high hydrophobicity with optimum surface roughness. Originality/value: Application of different alkyl chain groups of silane resin blending with micro- and nanoparticles of Si pigments develops superhydrophobic coatings with high thermal stability. © 2018, Emerald Publishing Limited. |
|---|