Evaluation on the physical and mechanical properties of particleboard from batai (Paraserianthes falcataria) / Noor Rehan Ismail, Siti Noorbaini Sarmin and Jamaludin Kasim

• Main Authors: Ismail, Noor Rehan, Sarmin, Siti Noorbaini, Kasim, Jamaludin
• Format: Conference or Workshop Item
• Language: English
• Published: 2011
• Subjects: Timber; Malaysia; Engineered wood. Fiberboard, particle board, etc.
• Online Access: https://ir.uitm.edu.my/id/eprint/57891/1/57891.PDF; https://ir.uitm.edu.my/id/eprint/57891/

The objective of this study was to investigate the suitability of Batai wood (Paraserianthes falcataria) in manufacture of particleboard. In this study, Urea Formaldehyde (UF) was used as a binder with three different resin content; 8%, 10% and 12% with/without addition 1% of wax. Two different particles size; 1.0 mm and 2.0 mm were used. The target density was 550kg/m2 . The properties include Bending Strength (MOR and MOE), Internal Bond Strength and water absorption were determined based on Japanese International Standard (JIS). From the study, it showed that, MOR and MOE value for panel with size 2.0mm is greater compare with 1.0mm. Conversely, panel manufactured using 1.0mm was better in internal bond strength compare with panel 2.0mm. The result also shows that, MOR, MOE and internal bond strength for panel without wax is higher compare with panel with wax. The percentage of resin contain also affected the bending strength of the panel. When the percentage of resin increased, the MOR and MOE value was increased. The water absorption rate for panel with addition of wax using 1.0mm particle was slightly lower compare with panel manufactured without wax. Particles sizes, percentage of resin contain and addition of wax were affected the mechanical properties of particleboard from Batai.