Observation on void formed in oxide scale of Fe-Cr-Ni alloy at 1073K in dry and humid environments
Void formation in oxide scale during high temperature oxidation is a common phenomenon.Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. W...
Saved in:
Main Authors: | Akhbar, Kaderi, Ani, Mohd Hanafi, Othman, Raihan, Mohd Zainal, Ahmad Zaki |
---|---|
Format: | Conference or Workshop Item |
Language: | English |
Published: |
2011
|
Subjects: | |
Online Access: | http://irep.iium.edu.my/4128/1/Observation_on_Void_Formed_in_Oxide_Scale_of_Fe-Cr-Ni_Alloy_at_1073_K_in_Dry_and_Humid_Environments.pdf http://irep.iium.edu.my/4128/ http://ucitv.uthm.edu.my/ucitveos53/Viewer/?peid=a705eae1-7b99-4dd3-8f15-57829cd17a24 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Similar Items
-
Observation on void formed in oxide scale of Fe-Cr-Ni alloy at 1073K in dry and humid environments
by: Kaderi, Akbar, et al.
Published: (2011) -
The effect of water vapor on high temperature oxidation
of Fe-Cr alloys at 1073K
by: Ani, Mohd Hanafi, et al.
Published: (2009) -
The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
by: Ani, Mohd Hanafi, et al.
Published: (2012) -
Increase of oxygen permeability on metal/oxide interface during high temperature oxidation of Fe-Cr alloys in water vapor at 1073 K
by: Ani, Mohd Hanafi, et al.
Published: (2010) -
Effects of water vapor on protectiveness of Cr2O3 scale
at 1073 k
by: Arifin, S. K., et al.
Published: (2017)