Comparative study on the wears of ZTA-TiO2-Cr2O3 ceramic cutting tool and commercial ceramic cutting tool

• Main Authors: Mudzaffar, Raqibah Najwa, Manshor, Hanisah, Ahmad Azhar, Ahmad Zahirani, Rejab, Nik Akmar, Mohd Ali, Afifah
• Format: Proceeding Paper
• Language: English; English
• Published: Trans Tech Publications Ltd 2022
• Subjects: QC Physics
• Online Access: http://irep.iium.edu.my/111113/1/111113_Comparative%20study%20on%20the%20wears%20of%20ZTA-TiO2-Cr2O3.pdf; http://irep.iium.edu.my/111113/2/111113_Comparative%20study%20on%20the%20wears%20of%20ZTA-TiO2-Cr2O3_SCOPUS.pdf; http://irep.iium.edu.my/111113/; https://www.scientific.net/KEM.908.196

The ZTA-TiO2-Cr2O3 ceramic cutting tool is a new cutting tool that possesses good hardness and fracture toughness. Yet, the performance of the ZTA-TiO2-Cr2O3 cutting tool is still unknown and needs further study. In this research, the comparison of the ZTA-TiO2-Cr2O3 and Kennametal ceramic cutting tool is investigated. The turning process by using ZTA-TiO2-Cr2O3 and Kennametal commercial ceramic cutting tools is performed on the Bridgeport ROMI PowerPath CNC lathe machine. The parameters utilized are spindle speed in the range of 907 to 1543 rpm, feed rate from 0.08 to 0.22 mm/rev, and depth of cut of 0.2 mm. Analysis of the flank wear and crater wear were performed by using an optical microscope (NIKON MM-4001L), while the chipping area was observed by scanning electron microscopy, SEM (JEOL JSM-IT100). The surface roughness of the machined surface is measured via portable surface roughness (Mahr MarSurf M3000C). The comparison between the cutting tool produced in this research and the commercial cutting tool shows that the wear performance of the ZTA-TiO2-Cr2O3 ceramic cutting tool is lower than the Kennametal commercial ceramic cutting tool. Even though this newly fabricated cutting tool is far behind compared to the commercial cutting tool, it shows some promising aspects such as the ability to cut at a higher speed.