Improved Procedure to Prevent Hydrogen Induced Cracking for Welding Offshore Structures
The objectives of the study are to study the causes of failure due to hydrogen induced cracking and its method of prevention and improve the current offshore welding procedure thus reduces the occurrence of hydrogen induced cracking in offshore repair works. The project covered the condition and pre...
Saved in:
Main Author: | Myra Azwinna Binti Sapian, Myra Azwinna |
---|---|
Format: | Final Year Project |
Language: | English |
Published: |
Universiti Teknologi Petronas
2009
|
Subjects: | |
Online Access: | http://utpedia.utp.edu.my/670/1/Myra_Azwinna_Final_Report.pdf http://utpedia.utp.edu.my/670/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Similar Items
-
Stress Corrosion Cracking on Welding of Offshore Structure
by: Azizdin, Amirul Iman Bin
Published: (2009) -
Effect of Chloride on Offshore Structure Welding Procedure
by: Zakaria Bin Mohamed, Zakaria
Published: (2009) -
Effects of absorbed hydrogen and thermal exposure on mechanical properties, crack opening and fatigue crack propagation of welded steel
by: Khattak, Muhammad Adil
Published: (2009) -
Effect of absorbed hydrogen on crack-tip ductility in the welded A516 steel
by: Khattak, M. A., et al.
Published: (2007) -
Effects of thermal aging and absorbed hydrogen on fatigue crack growth behavior of welded C-Mn steels
by: Khattak, Muhammad Adil, et al.
Published: (2013)