Chromium(III) based Ziegler-Natta catalysts for olefin polymerization

Four chromium based oxo-trinuclear carboxylate complexes were prepared by reacting chromium(III) nitrate nonahydrate with acetic acid and substituted carboxylic acids. They were characterized using infrared spectroscopy (FT-IR). Chromium content of the complexes was determined by titrimetry method....

Full description

Saved in:
Bibliographic Details
Main Authors: Wong .J.X,, Gan .S.N,, Aishah .M.J,
Format: Article
Language:English
Published: Universiti Kebangsaan Malaysia 2011
Online Access:http://journalarticle.ukm.my/2568/1/16_J.X._Wong.pdf
http://journalarticle.ukm.my/2568/
http://www.ukm.my/jsm/
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Four chromium based oxo-trinuclear carboxylate complexes were prepared by reacting chromium(III) nitrate nonahydrate with acetic acid and substituted carboxylic acids. They were characterized using infrared spectroscopy (FT-IR). Chromium content of the complexes was determined by titrimetry method. The chromium(III) monochloroacetate complex, [Cr3O(ClCH2COO)6.3H2O]NO3.3H2O in combination with diethylaluminium chloride formed heterogeneous catalyst system for ethylene polymerization. Both Al/Cr ratio and temperature influenced the catalytic activity. The maximum activity was 1768 gPE/gCr/hr/atm, achieved by polymerizing at 29°C and monomer pressure around 1 atm, with Al/Cr ratio 30.8. Effect of chloro-substituent groups on carboxylic ligand was studied by comparing the catalytic acitivities of chromium(III) monochloroacetate, chromium(III) dichloroacetate, chromium(III) trichloroacetate and chromium(III) acetate.The polymerization reaction was found to be first order with respect to the monomer during the initial stage. The activity decreases very rapidly presumably due to fast decay of the active sites. The polyethylene was characterized using FT-IR and DSC, and the results showed that it was of high density and crystallinity.