Influence of Chitosan nanoparticles on cellulose acetate film from durian rind

• Main Authors: Rachaporn Kudisri,, Tanat Uan-On,
• Format: Article
• Language: English
• Published: Penerbit Universiti Kebangsaan Malaysia 2019
• Online Access: http://journalarticle.ukm.my/14713/1/48_04_09.pdf; http://journalarticle.ukm.my/14713/; http://www.mabjournal.com/index.php?option=com_content&view=article&id=946&catid=59:current-view&Itemid=56

Cellulose acetate (CA) from durian rind and Chitosan nanoparticles (CSNPs) films were prepared in this study. The synthesis of CA from durian rind in a rapid process by a transesterification reaction. The structure of CA was characterized by FTIR. CSNPs were prepared by ionic gelation method with different concentrations of sodium tripolyphosphate (TPP). The particle size gradually decrease significantly when TPP concentration increases from 0.3% to 0.6%. The influence of the CSNPs on CA films was determined by measuring the tensile strength, whereby increases in the tensile strength and load at break were seen, with values of 4.38 ± 0.20 N/mm2 and 21.29 ± 0.98 N/mm2, respectively. At the optimum ratio of 0.975/0.025 (CA/ CSNPs) the particle size was 338 nm. Therefore, the influence of the CSNPs in the CA film could be explained, whereby increasing the size of the CSNPs, the adhesion is increased through the highly agglomerated fillers, which will be strongly bonded within the matrix. The CA/CSNPs films which could be reduce agricultural waste and increase the values. In the future, these nanocomposite films can be developed in the membrane to use wastewater treatment.