Interfacial reaction between SAC305 and SAC405 lead-free solders and electroless nickel/immersion silver (ENImAg) surface finish
The different surface finish and solder size on printed circuit board strongly affect the formation of intermetallic compounds (IMCs) and solder joint reliability. Among of various surface finish in the electronic industry, electroless nickel/immersion gold is the most popular at the moment. Howe...
保存先:
| 第一著者: | |
|---|---|
| フォーマット: | 学位論文 |
| 言語: | English English English |
| 出版事項: |
2017
|
| 主題: | |
| オンライン･アクセス: | http://eprints.uthm.edu.my/853/1/24p%20RABIATUL%20ADAWIYAH%20MOHAMED%20ANUAR.pdf http://eprints.uthm.edu.my/853/2/RABIATUL%20ADAWIYAH%20MOHAMED%20ANUAR%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/853/3/RABIATUL%20ADAWIYAH%20MOHAMED%20ANUAR%20WATERMARK.pdf http://eprints.uthm.edu.my/853/ |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | The different surface finish and solder size on printed circuit board strongly affect the
formation of intermetallic compounds (IMCs) and solder joint reliability. Among of
various surface finish in the electronic industry, electroless nickel/immersion gold is
the most popular at the moment. However, because their black pad issues, electroless
nickel/immersion silver (ENImAg) was developed as an alternative surface finish.
Therefore, the effect on an interfacial reaction between lead-free solder and ENImAg
surface finish using different solder ball size (Ø300μm, Ø500μm and Ø700μm) was
investigated. All samples were subjected to an aging process with different aging
times. The characterizations of IMC formation were examined by image analyzer,
scanning electron microscopy and energy dispersive x-ray. The results showed that
ENImAg finish was free from the black pad nickel. Subsequently, the solder ball size
has a significant effect on the IMC formation and fracture surface of as-reflowed and
aged solder joint. The IMC thickness of larger solder balls was found to be thicker
(1.74 μm) than smaller solder balls (1.32 μm) during soldering. In contrast to aged
solder joints, the smaller solder ball produced thicker (3.51 μm) IMC compared to
bigger solder balls (2.47 μm). Furthermore, the fracture surface of smaller solder ball
size showed ductile mode for both reflowed and aged solder joints. In addition, the
solder joint on ENImAg surface finish displayed a thinner layer and smaller grain sizes
compared to solder joint on bare copper. |
|---|