Crack growth analysis for rice husk reinforced polypropylene composite using equivalent initial flaw size concept
Crack growth that takes place in natural fibre polymer composite formations is dependent on several factors, whereby primary crack size is a key aspect that influences uncertainty of the crack growth. The nucleation stage is strongly affected by the fracture collapse of structures, unavoidably affec...