The effects of sintering behavior of zirconiadoped hydroxyapatite for clinical applications
Hydroxyapatite is one of the most potential bioceramic to be applied into the medical and dental field due to its biocompatibility with human hard tissue. However, its properties are still behind those of hard tissues and further studies need to be done to improve its mechanical properties. In the c...
保存先:
| 主要な著者: | , , , , , |
|---|---|
| その他の著者: | |
| フォーマット: | 論文 |
| 出版事項: |
Maney Publishing
2023
|
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | Hydroxyapatite is one of the most potential bioceramic to be applied into the medical and dental field due to its biocompatibility with human hard tissue. However, its properties are still behind those of hard tissues and further studies need to be done to improve its mechanical properties. In the current work, hydroxyapatite powder was prepared via the wet chemical method. Subsequently, the powder was doped with zirconia with weight percentages of 005, 01, 05, 1 and 5%. The bulks were then sintered at temperatures of 1100, 1200 and 1300°C at atmospheric pressure. The results revealed that the highest relative density of 999% was obtained for samples doped with 01% zirconia when sintered at 1200°C. Nevertheless, samples doped with 5 wt-% of zirconia showed relative lower relative densities regardless of sintering temperature. This was attributed by the presence of secondary phase which has cause decomposition during sintering. © W. S. Maney &Son Ltd 2014. |
|---|