Correlation of open cell structure with properties of green rubber foam from epoxidised natural rubber/reclaimed rubber glove / M.A. Mahamood...[et al.]

• Main Authors: M.A., Mahamood, N., Mohamad, A.R., Jeeffeerie, A.H., Mohd Zain
• Format: Article
• Language: English
• Published: Faculty of Mechanical Engineering Universiti Teknologi MARA (UiTM) 2017
• Subjects: TJ Mechanical engineering and machinery
• Online Access: http://ir.uitm.edu.my/id/eprint/37035/1/37035.pdf; http://ir.uitm.edu.my/id/eprint/37035/; https://jmeche.uitm.edu.my/

A promising impact absorber foam material was produced from epoxidised natural rubber (ENR) and reclaimed rubber (RR) with the addition of sodium bicarbonate (SBC) as a blowing agent. This study is part of our effort to develop green rubber foam from reclaimed rubber from glove. It focuses on the effect of different ENR/RR ratio of 100/0, 90/10, 70/30, 50/50, 30/70 and 0/100. The samples were prepared by melt compounding using a Haake internal mixer and expanded via two step heat transfer foaming process. The physical characteristics (expansion ratio, density and water absorption) and impact absorption by drop ball testing of ENR/RR foams were studied. The results showed significant correlation between the rubber blend ratios with generated pore structures towards the properties of the foams. From the experimental values, ENR/RR with the ratio of 90/10 yielded the rubber foam with the highest relative density of 0.85 as well as the lowest water absorption rate of 0.1 g/hrs. This foam cell characteristics resulted in improved energy absorption behaviour. Sample with optimum pore size of ~0.36 mm shows the highest energy absorption of up to 0.65 joules compared to others.