Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application
The characteristics of ZnO/PVA on the cotton in term of mechanical strength, surface morph ologies, chemical structure, composition , crystal size of ZnO and antibacterial performance were investigated Range of ZnO compositions ( 0.1, 0.15, 0.2, 0.25 M ) were cooperated with polyvinyl alcohol(PVA)...
Saved in:
Main Author: | |
---|---|
Format: | Final Year Project / Dissertation / Thesis |
Published: |
2018
|
Subjects: | |
Online Access: | http://eprints.utar.edu.my/3625/1/ESA%2D2019%2D1700216%2D1.pdf http://eprints.utar.edu.my/3625/ |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-utar-eprints.3625 |
---|---|
record_format |
eprints |
spelling |
my-utar-eprints.36252019-12-17T04:08:09Z Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application Tan, Lee Yae TP Chemical technology The characteristics of ZnO/PVA on the cotton in term of mechanical strength, surface morph ologies, chemical structure, composition , crystal size of ZnO and antibacterial performance were investigated Range of ZnO compositions ( 0.1, 0.15, 0.2, 0.25 M ) were cooperated with polyvinyl alcohol(PVA) solution (5, 10, 15, 20 g in 200 ml of water) The cotton was padded in the PVA/ZnO solution and dried it at 70 ℃ for overnight It was found that all the treated samples had abundant particles deposit ed on fibers and fibers are attached together. The corresponding EDX result showed carbon, oxygen and zinc elements presented on the treated cotton fabric. From EDX mapping, Zn element was presented uniformly over the cotton fabric. For XRD result, there w as peak at 31.96 31.96°, 34.66 34.66°, 36.46 36.46°, 47.92 47.92° and 56.73 56.73° attributed to the characteri stic peak of ZnO which revealed hexagonal wurtzite structure of the synthesized ZnO NPs. The crystal size of ZnO in the sample was calculated Debye Scherer formula was approxi mately 25~42 nm. Based on FTIR result, the decreasing order of hydroxyl peak of treated samples indicated the bonding was formed between ZnO, PVA and cotton. The antibacterial efficiencies against S.aureus and E.coli increase when ZnO and PVA dosage increase. Generally, t he optimal formulation of antibacterial cotton fabric at 0.25 M ZnO / 15 g PVA as the coated fabric has highest strength against tearing and considerable antibacterial properties against S. aureus and E. coli growth. 2018 Final Year Project / Dissertation / Thesis NonPeerReviewed application/pdf http://eprints.utar.edu.my/3625/1/ESA%2D2019%2D1700216%2D1.pdf Tan, Lee Yae (2018) Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application. Master dissertation/thesis, UTAR. http://eprints.utar.edu.my/3625/ |
institution |
Universiti Tunku Abdul Rahman |
building |
UTAR Library |
collection |
Institutional Repository |
continent |
Asia |
country |
Malaysia |
content_provider |
Universiti Tunku Abdul Rahman |
content_source |
UTAR Institutional Repository |
url_provider |
http://eprints.utar.edu.my |
topic |
TP Chemical technology |
spellingShingle |
TP Chemical technology Tan, Lee Yae Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application |
description |
The characteristics of ZnO/PVA on the cotton in term of
mechanical strength, surface morph ologies, chemical structure, composition , crystal size of ZnO and antibacterial performance were investigated Range of ZnO
compositions ( 0.1, 0.15, 0.2, 0.25 M ) were cooperated with polyvinyl alcohol(PVA) solution (5, 10, 15, 20 g in 200 ml of water) The cotton was padded in the PVA/ZnO solution and dried it at 70 ℃ for overnight It was found that all the treated samples had abundant particles deposit ed on fibers and fibers are attached together. The corresponding EDX result showed carbon, oxygen and
zinc elements presented on the treated cotton fabric. From EDX mapping, Zn element was presented uniformly over the cotton fabric. For XRD result, there w as peak at 31.96 31.96°, 34.66 34.66°, 36.46 36.46°, 47.92 47.92° and 56.73 56.73° attributed to the characteri stic peak of ZnO which revealed hexagonal wurtzite structure of the
synthesized ZnO NPs. The crystal size of ZnO in the sample was calculated Debye Scherer formula was approxi mately 25~42 nm. Based on FTIR result, the decreasing order of hydroxyl peak of treated samples indicated the
bonding was formed between ZnO, PVA and cotton. The antibacterial efficiencies against S.aureus and E.coli increase when ZnO and PVA dosage increase. Generally, t he optimal formulation of antibacterial cotton fabric at
0.25 M ZnO / 15 g PVA as the coated fabric has highest strength against tearing and considerable antibacterial properties against S. aureus and E. coli growth. |
format |
Final Year Project / Dissertation / Thesis |
author |
Tan, Lee Yae |
author_facet |
Tan, Lee Yae |
author_sort |
Tan, Lee Yae |
title |
Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application |
title_short |
Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application |
title_full |
Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application |
title_fullStr |
Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application |
title_full_unstemmed |
Functionalization of Cotton Fabric With Zno/pva for Antibacterial Textile Application |
title_sort |
functionalization of cotton fabric with zno/pva for antibacterial textile application |
publishDate |
2018 |
url |
http://eprints.utar.edu.my/3625/1/ESA%2D2019%2D1700216%2D1.pdf http://eprints.utar.edu.my/3625/ |
_version_ |
1657491980768247808 |
score |
13.1944895 |